Assessment of bonding durability of CLT and glulam made from oak and mixed poplar-oak according to bonding pressure and glue type
Article dans une revue avec comité de lecture
Date
2022-06-13Journal
Construction and Building MaterialsRésumé
The objective of this study is to evaluate the influence of manufacturing parameters on the bonding quality of CLT and glulam made from oak and mixing poplar and oak species. Studied bonding parameters were bonding pressure and glue type. To test the bonding durability, the specimens were subjected to a vacuum pressure cycle followed by drying to the initial weight. The bonding quality was then measured from delamination, residual shear strength, and wood failure percentage (WFP). Bonding pressure and type of glue appeared to have a significant influence on the bonding quality of CLT or glulam, with also significant interactions with the kind of species bonded. If a 0.8 N/mm² bonding pressure seemed to provide better results, vacuum-pressed (0.085 N/mm² bonding pressure) mixed poplar-oak CLT or glulam glued with PUR were very close to reaching the requirements of the standards. Generally, CLT or glulam entirely made from oak delaminated more than the mixed specimens. However, their residual shear strength can be comparable or even superior to what was obtained with mixed poplar-oak specimens. As a result, residual shear strength after delamination test may be interesting to consider as an additional criterion to assess glue line integrity of hardwood CLT or glulam products.
Fichier(s) constituant cette publication
- Nom:
- LaBoMaP_ConBuiMat_2022_POT.pdf
- Taille:
- 925.1Ko
- Format:
- Description:
- Manuscrit
- Fin d'embargo:
- 2022-12-13
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lectureLONGUETAUD, Fleur; POT, Guillaume; MOTHE, Frédéric; BARTHELEMY, Alexis; DECELLE, Rémi; DELCONTE, Florian; GE, Xihe; GUILLAUME, Grégoire; MANCINI, Théo; RAVOAJANAHARY, Tojo; BUTAUD, Jean-Claude; COLLET, Robert; DEBLED-RENNESSON, Isabelle; MARCON, Bertrand; NGO, Phuc; ROUX, Benjamin; VIGUIER, Joffrey (Springer Science and Business Media LLC, 2022-11-28)The TreeTrace_Douglas database includes images and measurements at several stages of the processing of Douglas fir logs, from sawmill logyard to machine grading and destructive testing of boards, and is suitable for research ...
-
Communication avec acteDURIOT, Robin; FRAYSSINHES, Rémy; RESCALVO, Francisco J.; COTTIN, Fabrice; BUTAUD, Jean-Claude; DENAUD, Louis; COLLET, Robert; POT, Guillaume; GIRARDON, Stéphane (2019)Selon un rapport rendu au Sénat le 26 juin 2019, le vieillissement du patrimoine des ponts du réseau routier est un problème à traiter en France. Le remplacement progressif d’environ 10% de ces ouvrages est à envisager dès ...
-
Communication avec actePENVERN, Hélène; POT, Guillaume; VIGUIER, Joffrey; COLLET, Robert; DEMOULIN, Leyne; ROUX, Benjamin; OLSSON, Anders; HU, Min (2023-09-05)This work is exhibiting a new laboratory investigation method to obtain fibre 3D angle measurement of a wood piece after successive planing of the whole specimen. By combining in-plane fibre measurements through laser ...
-
Article dans une revue avec comité de lectureDAVAL, Vincent; BELKACEMI, Mohamed; MERIAUDEAU, Fabrice; COLLET, Robert; POT, Guillaume (Optical Society of America - OSA Publishing, 2015)In this paper, a new approach to computing the deviation of wood grain is proposed. To do this, the thermal conduction properties of timber are used (higher conduction in the fiber direction). Exciting the surface of the ...