Cobalt-based superalloy layers deposited on X38CrMoV5 steel base metal by explosion cladding process
Article dans une revue avec comité de lecture
Abstract
A grade 25 cobalt-based superalloy in the form of a sheet 5 mm in thickness and a steel substrate of type X38CrMoV5 are joined by explosion cladding. The macrostructure and microstructure of the interface and of the co-based superalloy layers are studied. The interface presents the form of wavelets with a period of 1000 µm and an amplitude of 250 µm. The superalloy grains are deformed during the cladding process with several slip systems appearing. Near to the interface, the superalloy grains elongate and tend to follow the geometry of the interface. Observation with a scanning electron microscope (SEM) reveals zones of localised fusion at the interface. The EDS analysis shows that these fusion zones are the result of mixing between the base and cladding plates. Radiocrystallographic analysis by X-ray diffraction reveals the presence of the f.c.c cobalt in the cobalt-based superalloy layer. Thus cobalt retains its crystallographic structure (f.c.c) after cladding process. Hardness is evaluated with reference to microstructure. Near the interface, the hardness of the superalloy is of the order of 600 HV1 kg. In the remainder of the thickness, hardness is of the order of 500 HV1 kg, being greater than that of the unplated superalloy (270 HV1 kg). The track obtained by an indentation test at the interface under a load of 100 kg exhibits no cracking. This tends to prove the good metallurgical bond at the interface.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lectureJEMAL, Nejah; ZIMMER-CHEVRET, Sandra; LANGLOIS, Laurent; ABBA, Gabriel (Trans Tech Publications, 2013)Friction stir welding is known for his capability to achieve a linear weld. However, more investigation on a curved friction stir weld trajectory is still required to industrialize this promising process. In the same ...
-
Communication avec acteNGUYEN, Von Dim; MARTIN, Patrick; LANGLOIS, Laurent; CROUE, Jean-Baptiste (Springer, 2014)As a solution for traditional design process having many drawbacks in the manufacturing process, the integration of Product design-Process selection-Process planning is carried out in the early design phase. The technological, ...
-
Rapport de rechercheZIMMER-CHEVRET, Sandra; LANGLOIS, Laurent; BEN ATTAR, Amarilys (ABBA Gabriel, 2014)Ce document traite de la modélisation des actions mécaniques entre l’outil et la matière. L’objectif est de définir un modèle exploitable pour la définition de la commande du robot. Dans un premier temps, le rapport présente ...
-
Rapport de rechercheJEMAL, Nejah; BEN ATTAR, Amarilys; LANGLOIS, Laurent; ZIMMER-CHEVRET, Sandra (2014)En soudage par friction malaxage (Friction Stir Welding, FSW), l’outil est l’acteur principal de l’opération. Dans sa configuration conventionnelle, l’outil FSW n’est pas considéré comme un consommable lors du soudage des ...
-
Communication avec acteLANGLOIS, Laurent; CROUE, Jean-Baptiste; DELAMEZIERE, Arnaud; MARTIN, Patrick; ZIMMER-CHEVRET, Sandra (AIP PRIMECA, 2012)Le procédé de soudage FSW est un procédé relativement récent dont le premier brevet date de 1991. Ses principaux avantages proviennent du fait qu’il permet de réaliser des soudures à l’état solide de proche en proche. Ceci ...