Effect of interlamellar spacing on the elastoplastic behavior of C70 pearlitic steel: Experimental results and self-consistent modeling
Article dans une revue avec comité de lecture
Date
2014Journal
Materials and DesignAbstract
The effect of pearlite microstructure characteristics on strength and deformation of C70 pearlitic steel was investigated. Tensile tests under X-ray diffraction coupled with self-consistent model have been used to identify the role of interlamellar spacing on the ferrite plasticity parameters and residual stress induced by plasticity. Tests have been carried out on two pearlitic microstructures with interlamellar spacing Sp = 170 and 230 nm respectively. Ferrite critical shear stresses ðs0c ðaÞÞ are equal to 75–86 MPa for interlamellar spacing Sp = 230 nm and 105–120 MPa for interlamellar spacing Sp = 170 nm. Moreover, the compressive residual stress measured in ferrite phase is higher in elasto-plastically deformed sample (total strain of E11 = 1.2%) having larger interlamellar spacing (rR Fea ¼ 161 MPa for Sp = 230 nm and rR Fea ¼ 77 MPa for Sp = 170 nm).
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lectureMARCISZKO, Marianna; WAWSZCZAK, Roman; SIDHOM, Habib; BRAHAM, Chedly; WROBEL, Mirosław; WRONSKI, Sebastian; OPONOWICZ, Adrian; GENZEL, Christoph; KLAUS, Manuela; BACZMANSKI, Andrzej (International Union of Crystallography, 2018)The main focus of the presented work was the investigation of structure and residual stress gradients in the near-surface region of materials studied by X-ray diffraction. The multireflection method was used to measure ...
-
Article dans une revue avec comité de lectureBACZMANSKI, Andrzej; ZHAO, Yuchen; GADALIŃSKA; LE JONCOUR, Lea; WROŃSKI, Sebastian; BRAHAM, CHEDLY; PANICAUD, Benoît; FRANÇOIS, Manuel; BUSLAPS, Thomas; SOLODUCHA, K.a (Elsevier, 2016)The paper deals with damage and fracture behavior of ductile metals caused by stress-state-dependent growth and coalescence of defects on the micro-level. The continuum damage model has been generalized to take into account ...
-
Article dans une revue avec comité de lectureBACZMANSKI, Andrzej; ZHAO, Yuchen; GADALIŃSKA, E; LE JONCOUR, Léa; WROŃSKI, Sebastian; PANICAUD, Benoît; BRAHAM, Chedly; FRANÇOIS, Manuel; BUSLAPS, Thomas; SOLODUCHA, K. (Elsevier, 2016)In situ time of flight neutron diffraction and X-ray synchrotron diffraction methods were applied to measure lattice strains in duplex steels during a tensile test. The experimental results were used to study slips on ...
-
Article dans une revue avec comité de lectureLE JONCOUR, Léa; PANICAUD, Benoît; BACZMANSKI, Andrzej; FRANÇOIS, Manuel; BRAHAM, Chedly; PARADOWSKA, Anna Maria; WROŃSKI, Sebastian; CHIRON, Rémi (Elsevier, 2010)Different experimental approaches have been performed in order to extract damage at several scales. In this paper two experimental methods are treated. Neutron diffraction coupled with tensile test has been performed to ...
-
Article dans une revue avec comité de lectureMARCISZKO, Marianna; BACZMANSKI, Andrzej; BRAHAM, Chedly; WROBEL, Mirosław; WRONSKI, Sebastian; CIOS, Grzegorz (Elsevier, 2017)The presented study introduces the development of the multi-reflection grazing-incidence X-ray diffraction method (MGIXD) for residual stress determination. The proposed new methodology is aimed at obtaining more reliable ...