Effect of interlamellar spacing on the elastoplastic behavior of C70 pearlitic steel: Experimental results and self-consistent modeling
Article dans une revue avec comité de lecture
Date
2014Journal
Materials and DesignAbstract
The effect of pearlite microstructure characteristics on strength and deformation of C70 pearlitic steel was investigated. Tensile tests under X-ray diffraction coupled with self-consistent model have been used to identify the role of interlamellar spacing on the ferrite plasticity parameters and residual stress induced by plasticity. Tests have been carried out on two pearlitic microstructures with interlamellar spacing Sp = 170 and 230 nm respectively. Ferrite critical shear stresses ðs0c ðaÞÞ are equal to 75–86 MPa for interlamellar spacing Sp = 230 nm and 105–120 MPa for interlamellar spacing Sp = 170 nm. Moreover, the compressive residual stress measured in ferrite phase is higher in elasto-plastically deformed sample (total strain of E11 = 1.2%) having larger interlamellar spacing (rR Fea ¼ 161 MPa for Sp = 230 nm and rR Fea ¼ 77 MPa for Sp = 170 nm).
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lectureMARCISZKO, Marianna; WAWSZCZAK, Roman; SIDHOM, Habib; WROBEL, Mirosław; WRONSKI, Sebastian; OPONOWICZ, Adrian; GENZEL, Christoph; KLAUS, Manuela; BACZMANSKI, Andrzej; BRAHAM, Chedly (International Union of Crystallography, 2018)The main focus of the presented work was the investigation of structure and residual stress gradients in the near-surface region of materials studied by X-ray diffraction. The multireflection method was used to measure ...
-
Article dans une revue avec comité de lectureMARCISZKO-WIACKOWSKA, M; BACZMANSKI, Andrzej; BRAHAM, Chedly; WATROBA, M.; WRONSKI, Sebastian; WAWSZCZAK, R.; GONZALEZ, Gonzalo; KOT, Piotr; KLAUS, Manuela; GENZEL, Christoph (Elsevier, 2023-06)In the presented research, the intergranular elastic interaction and the second-order plastic incompatibility stress in textured ferritic and austenitic steels were investigated by means of diffraction. The lattice strains ...
-
Article dans une revue avec comité de lectureMARCISZKO-WIĄCKOWSKA, M.; OPONOWICZ, A.; WĄTROBA, M.; WRÓBEL, M.; KLAUS, M.; GENZEL, Ch.; BACZMANSKI, Andrzej; BRAHAM, Chedly (2022-05)The choice of the grain interaction model is a critical element of residual stress analysis using diffraction methods. For the near-surface region of a mechanically polished austenitic steel, it is shown that the application ...
-
Article dans une revue avec comité de lectureBACZMANSKI, Andrzej; ZHAO, Yuchen; GADALIŃSKA; LE JONCOUR, Lea; WROŃSKI, Sebastian; PANICAUD, Benoît; FRANÇOIS, Manuel; BUSLAPS, Thomas; SOLODUCHA, K.a; BRAHAM, Chedly (Elsevier, 2016)The paper deals with damage and fracture behavior of ductile metals caused by stress-state-dependent growth and coalescence of defects on the micro-level. The continuum damage model has been generalized to take into account ...
-
Article dans une revue avec comité de lectureMARCISZKO, Marianna; BACZMANSKI, Andrzej; MIROSŁAW, Wrobel; SEILER, Wilfrid; WRONSKI, Sebastian; WAWSZCZAK, Roman; BRAHAM, Chedly (International Union of Crystallography, 2015)Multireflection grazing-incidence X-ray diffraction (MGIXD) was used to determine the stress- and strain-free lattice parameter in the surface layer of mechanically treated (polished and ground) tungsten and austenitic ...