Thermal oxidation of epoxies: Influence of diamine hardener
Article dans une revue avec comité de lecture
Date
2016Journal
Polymer Degradation and StabilityRésumé
This work reports the thermal oxidation of DGEBA resins totally cured with cycloaliphatic (isophorone diamine) or with linear aliphatic (trioxa-tridecanediamine or TTDA) diamine hardener. Chemical changes (carbonyl build-up) were monitored by FTIR and macromolecular changes (chains scission and crosslinking) from Tg variations measured by DSC. Exposition at several temperatures and under several oxygen pressures showed that DGEBA/IPDA has systematically the highest oxidation rate. It was also observed that DGEBA/IPDA undergoes mainly chain scissions whereas DGEBA/TTDA undergoes a predominant crosslinking under air being partially suppressed under enhanced oxygen pressure. Results were discussed on the basis of the possible influence of the structure of hardener.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lectureDJOUANI, Fatma; VERDU, Jacques; FLACONNECHE, Bruno; FAYOLLE, Bruno; RICHAUD, Emmanuel (Institut Français du Pétrole, 2015)This paper deals with polymer-fuel interaction focusing on specific effects of biofuels on polyethylene (PE) in automotive applications. The practical objective is to develop a predictable approach for durability of ...
-
Article dans une revue avec comité de lectureOKAMBA-DIOGO, Octavie; VERDU, Jacques; FERNAGUT, François; GUILMENT, Jean; PERY, Frédérique; FAYOLLE, Bruno; RICHAUD, Emmanuel (Elsevier, 2016)Polyamide 11 films stabilized by Irganox® 1098, Irganox® 1010 or Irganox® 245 were subjected to thermal oxidation at 110°C. The residual phenol content was assessed by comparing three analytical methods:high performance ...
-
Article dans une revue avec comité de lectureThe thermal oxidative ageing of vinyl ester and unsaturated polyester was studied at temperatures ranging from 120 to 160°C and oxygen pressures ranging from 0.02 to 2.0 MPa. The oxidation of both materials was shown to ...
-
Article dans une revue avec comité de lectureThermal oxidation of three epoxy resins prepared from flexible or rigid prepolymers and hardeners was studied by monitoring epoxy mechanical and physical changes. The physical changes were followed by mass measurements, ...
-
Article dans une revue avec comité de lectureThis work deals with a study of stabilizers loss by extraction in ethanol–cyclohexane mixtures simulating ethanol based biofuels. As theoretically predicted, cyclohexane has an extractive power considerably stronger than ...