A Thermodynamic and experimental study of low-alloy steels after carbonitriding in a low-pressure atmosphere
Article dans une revue avec comité de lecture
Auteur
MARRAY, TarekJACQUET, PhilippeMANSORI, MohammedFABRE, AgnèsBARRALLIER, LaurentRésumé
The effect of the composition of two steels (B and 6MnCr5) on precipitation of undesirable phases (carbides, nitrides and carbonitrides) under thermochemical treatment (low-pressure or vacuum carbonitriding) is investigated. Metallographic and x-ray diffraction studies and thermodynamic computations are performed.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Communication sans acte; ;
JÉGOU, Sébastien (2014)
Le rodage est un phénomène présent lors des premiers cycles de frottement qui modifie la surface de contact d’une pièce d’un point de vue géométrique, couplé à des modifications de propriétés mécaniques. Le rodage génère ... -
Communication sans acte; ;JÉGOU, Sébastien (2014)
In a previous study, the capability of X-ray diffraction technique to qualify damage occurring during friction had been proven [1]. The purpose of this study is to complete this research in order to develop a method to ...
-
Article dans une revue avec comité de lecture(Elsevier, 2013)Micropitting is a form of surface fatigue damage that occurs in the gear teeth. It is due to the effect of variation in the mechanical loading in the contact zone between the two teeth, induced especially by flank roughness. ...
-
Communication sans acte; ;JÉGOU, Sébastien (2014)
In a previous study, the capability of X-ray diffraction technique to qualify damage occurring during friction had been proven [1]. The purpose of this study is to complete this research in order to develop a method to ...
-
Article dans une revue avec comité de lecture(Elsevier, 2019)This paper describes a model developed to simulate the evolution of carbide layers (TaC/Ta2C) formed during carburizing and annealing treatments of tantalum. The model is based on a parabolic evolution of the layer thickness ...