Origin of epoxies embrittlement during oxidative ageing
Article dans une revue avec comité de lecture
Date
2017Journal
Polymer TestingAbstract
Thermal oxidation of three epoxy resins prepared from flexible or rigid prepolymers and hardeners was studied by monitoring epoxy mechanical and physical changes. The physical changes were followed by mass measurements, glass transition temperature using DSC and sub-glass β transition using DMA. It was put in evidence that embrittlement is not directly associated to Tg or mass loss changes since epoxy network based on isophorone diamine (IPDA) hardeners were shown to undergo mainly a chain scission at the beginning of exposure process whereas epoxy network based on trioxatridecane diamine (TTDA) hardeners exhibits a crosslinking process with a significant mass loss. The only common feature for both epoxy systems to understand embrittlement is the drop of amplitude of β transition with oxidation.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lectureDJOUANI, Fatma; VERDU, Jacques; FLACONNECHE, Bruno; FAYOLLE, Bruno; RICHAUD, Emmanuel (Institut Français du Pétrole, 2015)This paper deals with polymer-fuel interaction focusing on specific effects of biofuels on polyethylene (PE) in automotive applications. The practical objective is to develop a predictable approach for durability of ...
-
Article dans une revue avec comité de lectureOKAMBA-DIOGO, Octavie; VERDU, Jacques; FERNAGUT, François; GUILMENT, Jean; PERY, Frédérique; FAYOLLE, Bruno; RICHAUD, Emmanuel (Elsevier, 2016)Polyamide 11 films stabilized by Irganox® 1098, Irganox® 1010 or Irganox® 245 were subjected to thermal oxidation at 110°C. The residual phenol content was assessed by comparing three analytical methods:high performance ...
-
Article dans une revue avec comité de lectureThe thermal oxidative ageing of vinyl ester and unsaturated polyester was studied at temperatures ranging from 120 to 160°C and oxygen pressures ranging from 0.02 to 2.0 MPa. The oxidation of both materials was shown to ...
-
Article dans une revue avec comité de lectureThis work reports the thermal oxidation of DGEBA resins totally cured with cycloaliphatic (isophorone diamine) or with linear aliphatic (trioxa-tridecanediamine or TTDA) diamine hardener. Chemical changes (carbonyl build-up) ...
-
Article dans une revue avec comité de lectureThis work deals with a study of stabilizers loss by extraction in ethanol–cyclohexane mixtures simulating ethanol based biofuels. As theoretically predicted, cyclohexane has an extractive power considerably stronger than ...