Thermal and radio-oxidation of epoxy coatings
Article dans une revue avec comité de lecture
Auteur
GALANT, CKUNTZ, M.VERDU, Jacques 
FAYOLLE, BrunoRésumé
Degradation induced by thermal (50-110 °C) and radio-oxidation of low T g epoxy-amine networks has been studied. It has been found that oxidation leads mainly to amide groups formation at the vicinity of tertiary amines whatever ageing conditions (thermal or radio-oxidation at 200 Gy h -1 ). In addition, some species as acids, peracids or formates have been revealed indicating a chain scission process. Physical modifications as T g decrease and soluble fraction increase due to chain scission process, have been correlated with chemical modifications.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lecture; ; ;FAYOLLE, Bruno; RICHAUD, Emmanuel (Institut Français du Pétrole, 2015)
This paper deals with polymer-fuel interaction focusing on specific effects of biofuels on polyethylene (PE) in automotive applications. The practical objective is to develop a predictable approach for durability of ...
-
Article dans une revue avec comité de lecture; ; ; ;FAYOLLE, Bruno (Elsevier, 2014)
Thermal oxidation in air at atmospheric pressure, in the 80-140 °C temperature range and in oxygen at 100 °C in the 0.02-3 MPa pressure range, of unvulcanized, unstabilized, unfilled polychloroprene (CR) has been characterized ...
-
Article dans une revue avec comité de lecture;FAYOLLE, Bruno; RICHAUD, Emmanuel (Elsevier, 2011)
This article deals with polypropylene stabilization by hindered 2,6-di-tert-butylphenols. Two aspects are mainly considered: the influence of stabilizer structure, of its concentration and temperature on induction period ...
-
Article dans une revue avec comité de lecture; ; ; ;FAYOLLE, Bruno (Elsevier, 2014)
Water sorption has been studied gravimetrically for polychloroprene rubber samples, first at a fixed hygrometric ratio (98% HR) and several temperatures (25, 40, 60 and 80 °C) for samples of 1.8 and 3.8 mm thickness (Constant ...
-
Article dans une revue avec comité de lecture; ; ; ;FAYOLLE, Bruno (Elsevier, 2014)
tThe thermo-oxidative behavior of unformulated (unfilled) samples of epoxy coatings has been studiedat five temperatures ranging from 70◦C to 150◦C. Two epoxy networks based on diglycidyl ether ofbisphenol A (DGEBA), ...