Multiscale damage analysis of the tension‐tension fatigue behavior of a low‐density sheet molding compound
Article dans une revue avec comité de lecture
Date
2021Journal
Journal of Applied Polymer ScienceRésumé
This article presents the experimental findings of tension-tension stress-controlled fatigue tests performed on low-density sheet molding compound (LD-SMC). LD-SMC composite is a type of SMC including a polyester resin reinforced with chopped glass fibers bundles and hollow glass spheres. The coupled frequency-amplitude affects the nature of the overall fatigue response, which can be controlled by the damage mechanisms accumulation and/or by the self-heating. In fact, the self-heating produced a material softening and decreased the fatigue lifetime. For fatigue loading at 80 Hz, self-heating has been observed and yielded to a temperature rise to 65°C, which is more than a glass transition temperature of polyester. Thus, the polyester matrix is subjected to remarkable thermally activated modifications of its physical state. Multiscale damage analysis of the randomly-oriented sample in fatigue showed that the first observed damage phenomenon corresponds to the debonding of the hollow glass microspheres occurring in the fiber depleted zones.
Fichier(s) constituant cette publication
- Nom:
- PIMM_JAPS_2021_ SHIRINBAYAN.pdf
- Taille:
- 3.528Mo
- Format:
- Description:
- Article
- Fin d'embargo:
- 2021-07-01
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lectureSHIRINBAYAN, Mohammadali; ABBASNEZHAD, Navideh; SUROWIEC, Benjamin;
TCHARKHTCHI, Abbas;
FITOUSSI, Joseph;
MERAGHNI, Fodil (Elsevier, 2017)
This paper presents the results of an overall experimental characterization of the mechanical behavior of a Low Density Sheet Molding Compound (LD-SMC). LD-SMC is a polyester matrix containing mineral charge (CaCO3) ... -
High strain rate visco-damageable behavior of Advanced Sheet Molding Compound (A-SMC) under tension Article dans une revue avec comité de lectureSHIRINBAYAN, Mohammadali; SUROWIEC, Benjamin; BOCQUET, Michel;
TCHARKHTCHI, Abbas;
FITOUSSI, Joseph;
MERAGHNI, Fodil (Elsevier, 2015)
Advanced Sheet Molding Compound (A-SMC) is a serious composite material candidate for structural automotive parts. It has a thermoset matrix and consists of high weight content of glass fibers (50% in mass) compared to ... -
Article dans une revue avec comité de lectureABDALLAH-ELHIRTSI, Sofiane; EBRAHIMI, Kambiz; SHIRINBAYAN, Mohammadali; FARZANEH, Sedigheh;
TCHARKHTCHI, Abbas;
FITOUSSI, Joseph (MDPI, 2014)
In this study some new concepts regarding certain aspects related to shape memory polymers are presented. A blend of polylactic acid (PLA) (80%) and polybutylene succinate (PBS) (20%) was prepared first by extrusion, then ... -
High strain rate visco-damageable behavior of Advanced Sheet Molding Compound (A-SMC) under tension Article dans une revue avec comité de lectureSHIRINBAYAN, Mohammadali; SUROWIEC, Benjamin; BOCQUET, Michel;
TCHARKHTCHI, Abbas;
FITOUSSI, Joseph;
MERAGHNI, Fodil (Elsevier, 2015)
Advanced Sheet Molding Compound (A-SMC) is a serious composite material candidate for structural automotive parts. It has a thermoset matrix and consists of high weight content of glass fibers (50% in mass) compared to ... -
Conférence invitéeSHIRINBAYAN, Mohammadali; SUROWIEC, Benjamin; BOCQUET, Michel;
TCHARKHTCHI, Abbas;
FITOUSSI, Joseph;
MERAGHNI, Fodil (2015)
Advanced Sheet Molding Compound (A-SMC) is a serious composite material candidate for structural automotive parts. It has a thermoset matrix and consists of high weight content of glass fibers (50% in mass) compared to ...