Physico-chemical approach of polymer chemical ageing: a short review
Article dans une revue avec comité de lecture
Author
RICHAUD, EmmanuelAbstract
Polymers are known to degrade in their use conditions, with the risk that their properties reach unacceptable level. This paper reviews the modeling of modifications occurring at molecular and architectural changes occurring during their chemical ageing, with the aim of predicting the physical (mechanical) properties, all values being linked by structure properties relationships
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lecture; ;FAYOLLE, Bruno; RICHAUD, Emmanuel (Elsevier, 2016)
The thermal oxidative ageing of vinyl ester and unsaturated polyester was studied at temperatures ranging from 120 to 160°C and oxygen pressures ranging from 0.02 to 2.0 MPa. The oxidation of both materials was shown to ...
-
Article dans une revue avec comité de lecture; ; ; ; ; ;RICHAUD, Emmanuel (Elsevier, 2017)
The in situ thermal oxidation of thin unstabilized polydicyclopentadiene was studied by TGA to monitor mass gain, and DSC to characterize hydroperoxides concentration. Results were discussed using kinetic analysis, which ...
-
Article dans une revue avec comité de lecture; ; ; ; ; ;RICHAUD, Emmanuel (Elsevier, 2015)
This work aims to determine and understand the influence of UV weathering on the reprocessing of a wood-plastic composite (WPC), i.e. of a wood flour reinforced polypropylene (PP) composites. Two wood flour contents (10% ...
-
Article dans une revue avec comité de lecture; ; ;RICHAUD, Emmanuel (Wiley-VCH Verlag, 2014)
The hydrolysis of almost ideal networks based on macrodiols of average molar mass about 2 kg mol 1, with L¼18 ester groups per chain is studied. Tensile testing is used to evaluate the crosslink density through the statistical ...
-
Article dans une revue avec comité de lecture; ; ; ;FAYOLLE, Bruno; RICHAUD, Emmanuel (Elsevier, 2014)
The present article reports a study of thermal oxidation of unstabilized polyamide 11 films at several temperatures (90–165 °C) under atmospheric pressure and under various oxygen pressures (up to 1.6 MPa) at 110 °C. The ...