Crack initiation induced nanograins and facets of a titanium alloy with lamellar and equiaxed microstructure in very-high-cycle fatigue

Article dans une revue avec comité de lecture
Auteur
PAN, Xiangnan
303369 Chinese Academy of Sciences [Beijing] [CAS]
XU, Shouwen
303369 Chinese Academy of Sciences [Beijing] [CAS]
NIKITIN, Alexander
467316 National research university [MAI]
ccSHANYAVSKIY, Andrey
ccPALIN-LUC, Thierry
1002421 Institut de Mécanique et d'Ingénierie [I2M]
HONG, Youshi
262786 Chinese Academy of Geological Sciences [Beijing] [CAGS]

URI
http://hdl.handle.net/10985/24605
Date
2023
Journal
Materials Letters

Résumé

Fractographic and microstructure features in crack initiation region in very-high-cycle fatigue (VHCF) were characterized for an extruded titanium alloy VT3-1 under stress ratios R =–1 and 0.1. The material consists of lamellar and equiaxed microstructure. All specimens failed by internal crack initiation with rough area feature in VHCF. Within the rough area region, facets initiated from a big cluster of lamellar α at R = 0.1, and nanograin layers formed at some local areas underneath fracture surfaces due to insufficient contact of NCP (numerous cyclic pressing) process in the inhomogeneous microstructure at R = –1. Here, NCP mechanism still dominates the VHCF behavior of this titanium alloy under negative stress ratios, and facets dominate at R > 0.

Fichier(s) constituant cette publication

Nom:
PAN VT3-1-re-202311_preprint.doc
Taille:
2.118Mo
Format:
Microsoft Word
Description:
Preprint
Voir/Ouvrir

Cette publication figure dans le(s) laboratoire(s) suivant(s)