Hot Forging of a Cladded Component by Automated GMAW Process
Communication avec acte
Abstract
Weld cladding is employed to improve the service life of engineering components by increasing corrosion and wear resistance and reducing the cost. The acceptable multi-bead cladding layer depends on single bead geometry. Hence, in first step, the relationship between input process parameters and the single bead geometry is studied and in second step a comprehensive study on multi bead clad layer deposition is carried out. This paper highlights an experimental study carried out to get single layer cladding deposited by automated GMAW process and to find the possibility of hot forming of the cladded work piece to get the final hot formed improved structure. The experiments for single bead were conducted by varying the three main process parameters wire feed rate, arc voltage and welding speed while keeping other parameters like nozzle to work distance, shielding gas and its flow rate and torch angle constant. The effect of bead spacing and torch orientation on the cladding quality of single layer from the results of single bead deposition was studied. A hot bending test at different temperatures of cladded plates with different dilution and nominal energy carried out.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lectureThis paper focuses on the hot forging of multi-material cladded work pieces using upsetting tests. Thecase study corresponds to gas metal arc welding cladding of a SS316L on a mild steel (C15). Experimentaltests and ...
-
Communication avec acteThe presented work is dedicated to studying the forgeability of bimaterial cladded billet. Hot upsetting tests of cylindrical low carbon steel (C15) billets weld cladded (MIG) by stainless steel (SS316L) are experimentally ...
-
Cobalt-based superalloy layers deposited on X38CrMoV5 steel base metal by explosion cladding process Article dans une revue avec comité de lectureA grade 25 cobalt-based superalloy in the form of a sheet 5 mm in thickness and a steel substrate of type X38CrMoV5 are joined by explosion cladding. The macrostructure and microstructure of the interface and of the co-based ...
-
Article dans une revue avec comité de lectureThe distribution of liquid at the semi solid state is one of the most important parameters for steel thixoforging. It has a great influence on the viscosity of the material, on the flows and finally on the final shape and ...
-
Article dans une revue avec comité de lectureForging in semi-solid state significantly extends the possibilities of classical hot forging. In order to fully exploit its potential, the process requires a specific and demanding environment, penalizing its industrial ...