Fatigue Behavior of Polyamide 66/Glass Fiber Under Various Kinds of Applied Load
TypeArticles dans des revues avec comité de lecture
In this study, the fatigue behavior of polyamide 66 reinforced with short glass fibers and especially the role of glass fibers has been investigated under two kinds of cyclic loading. tension–tension fatigue tests with stress controlled and alternative flexural fatigue test with strain controlled were carried out. The main topics include microscope damage observation, described by fiber/matrix debonding and interfacial failure, endurance limit with Wohler curves, effect of self-heating temperature. For both tests, the surface temperature increases with an increasing applied load. The results show that the self-heating has an important effect in the failure point where the Wohler curves join each other. The fracture surface was analyzed by scanning electron microscope for both applied loads. The stress ratio is −1 for alternative flexural fatigue test and 0.1 and 0.3 for tension–tension fatigue test ones at frequencies ranging 2–60 Hz.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
ESMAEILLOU, Bardia; FEREIRRA, P; BELLENGER, Véronique; TCHARKHTCHI, Abbas (Wiley, 2012)Fatigue damage initiation of a PA66/glass fiber composite material is studied with interrupted tests carried out with an “alternative bending device” and a small applied strain. During the damage initiation period, no ...
TCHARKHTCHI, Abbas; FARZANEH, Sedigheh; ABDALLAH-ELHIRTSI, Sofiane; ESMAEILLOU, Bardia; NONY, Fabien; BARON, A (Taylor & Francis Online, 2014)This study concerns the effect of thermal aging on mechanical properties of polyurethane. Polyurethane samples were exposed at 85° and 120°C under inert atmosphere. Mechanical tests were carried out on these samples the ...
Micro-mechanisms of fatigue in short glass fiber reinforced polyamide 66: A multi-scale experimental analysis ESMAEILLOU, Bardia; FITOUSSI, Joseph; MERAGHNI, Fodil; TCHARKHTCHI, Abbas (2014)The objective of this work is to identify and to analyze the main micro-mechanisms which govern the fatigue behavior of a short glass fiber reinforced polyamide 66 composite through a multi-scale experimental analysis. ...
RICHAUD, Emmanuel; FERREIRA, Paulo; AUDOUIN, Ludmila; COLIN, Xavier; VERDU, Jacques; MONCHY-LEROY, Carole (Elsevier Ltd., 2010)Thin (60 μm) and thick (250 μm) samples of poly(ether ether ketone) were subjected to radiochemical ageing at 24 kGy h -1 dose rate for doses up to 30.7 MGy at 60 °C in air. FTIR spectrophotometry (hydroxyl and carbonyl ...
High strain rate visco-damageable behavior of Advanced Sheet Molding Compound (A-SMC) under tension SHIRINBAYAN, Mohammadali; FITOUSSI, Joseph; MERAGHNI, Fodil; SUROWIEC, Benjamin; BOCQUET, Michel; TCHARKHTCHI, Abbas (Elsevier, 2015)Advanced Sheet Molding Compound (A-SMC) is a serious composite material candidate for structural automotive parts. It has a thermoset matrix and consists of high weight content of glass fibers (50% in mass) compared to ...