Explanation of penetration depth variation during laser welding under variable ambient pressure
TypeArticles dans des revues avec comité de lecture
It has been observed that the penetration depth during laser welding (LW) under vacuum or reduced ambient pressure could be significantly greater than that during welding under atmospheric pressure. Previous explanations of this phenomenon usually limit to specific wavelength laser welding and have difficulties in explaining why the variation will disappear, as the welding speed increases. Here, we propose that this variation is caused by the temperature difference of keyhole wall under variable ambient pressure based on a correct physical description of related processes. A new surface pressure model, dependent on ambient pressure, is proposed for describing the evaporation process during laser material interaction under variable ambient pressure. For laser welding of a 304 stainless steel with 2.0kW laser power and 3m/min welding speed, it is shown that the average keyhole wall temperature is around 2900K under atmospheric pressure, and only around 2300K under vacuum, which results in significant penetration depth variations. Interestingly, it is also shown that as the welding speed increases, the average temperature of the front keyhole wall gradually rises due to the reduction of the mean incident angle of laser, and the magnitude of this increase is larger in welding under vacuum than under atmospheric pressure. It allows us to explain why the penetration depth improvement decreases to zero with the increase of welding speed;
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Temperature measurement of laser heated metals in highly oxidizing environment using 2D single-band and spectral pyrometry MULLER, Maryse; FABBRO, Rémy; EL-RABII, Hazem; HIRANO, Koji (Laser Institute of America, 2012)Calibration and validation of two temperature measurement techniques both using optical pyrometry, usable in the framework of the study of the heated metals in highly oxidizing environments and more generally during laser ...
Experimental determination of temperature threshold for melt surface deformation during laser interaction on iron at atmospheric pressure HIRANO, Koji; FABBRO, Rémy; MULLER, Maryse (IOP, 2011)Recoil pressure is the principal driving force of molten metal in laser processing in the intensity range of 10^-1 ~ 10^2 MW/cm2. It is thus essential to estimate the recoil pressure in order to describe physical processes ...
Possible explanations for different surface quality in laser cutting with 1 micron and 10 microns beams HIRANO, Koji; FABBRO, Rémy (AIP, 2012)In laser cutting of thick steel sheets, quality difference is observed between cut surfaces obtained with 1 micron and 10 micron laser beams. This paper investigates physical mechanisms for this interesting and important ...
HIRANO, Koji; FABBRO, Rémy (IOP, 2011)In laser cutting process, understanding of hydrodynamics of melt layer is significant, because it is an important factor which controls the final quality. In this work, we observed hydrodynamics of melt layer on kerf front ...
AMARA, El Hachemi; KHELOUFI, K; TAMSAOUT, T; FABBRO, Rémy; HIRANO, Koji (Springer, 2015)A theoretical approach based on a numerical simulation using experimental data is proposed as a contribution for the study of laser metal cutting under gas assistance. The aim is to simulate the stages of the kerf formation ...