Thermal response of DP600 dual-phase steel under ultrasonic fatigue loading
TypeArticles dans des revues avec comité de lecture
The present work employed in situ infrared thermography to investigate the thermal response and dissipative mechanisms of a dual-phase steel under ultrasonic tension-compression fatigue testing. A classical thermal response occurred for stress amplitudes below 247 MPa but an abnormal thermal response was observed for stress amplitudes above 247 MPa, in that the temperature stabilized after a steep increase of up to 350 °C. The mean dissipated energy per cycle was estimated based on temperature measurements using the heat diffusion equation. The relationship between the mean dissipated energy per cycle and the stress amplitude was studied, and mechanisms related to the observed thermal response were discussed.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Calorimetric Studies and Self-Heating Measurements for a Dual-Phase Steel Under Ultrasonic Fatigue Loading TORABIAN, Noushin; FAVIER, Véronique; ZIAEI-RAD, Saeed; DIRRENBERGER, Justin; ADAMSKI, Frédéric; RANC, Nicolas (ASTM International, 2016)The objective of the present research is to study the self-heating behavior of a dual-phase (DP) steel under ultrasonic fatigue loading and to investigate the effect of frequency on intrinsic heat dissipation of the material. ...
Self-Heating Measurements for a Dual-Phase Steel under Ultrasonic Fatigue Loading for stress amplitudes below the conventional fatigue limit TORABIAN, Noushin; FAVIER, Véronique; ZIAEI-RAD, Saeed; ADAMSKI, Frédéric; DIRRENBERGER, Justin; RANC, Nicolas (Elsevier, 2016)The aim of the present research was to study the self-heating behavior of a dual-phase steel under ultrasonic fatigue loading for stress amplitudes lower than the conventional fatigue limit. The steel studied in this ...
Correlation of the high and very high cycle fatigue response of ferrite based steels with strain rate-temperature conditions TORABIAN, Noushin; FAVIER, Véronique; DIRRENBERGER, Justin; ADAMSKI, Frédéric; ZIAEI-RAD, Saeed; RANC, Nicolas (Pergamon, 2017)The discrepancies observed between conventional and ultrasonic fatigue testing are assessed through the mechanisms of dislocation mobility in BCC metals. The existence of a transition condition between thermally-activated ...
PHUNG, Ngoc-Lam; FAVIER, Véronique; RANC, Nicolas; VALES, Fréderic; MURGHRABI, Haël (ELSEVIER, 2014)The surfaces of commercially pure polycrystalline copper specimens subjected to interrupted 20 kHz fatigue tests in the very high cycle fatigue regime were investigated. The stress amplitude needed to form the early slip ...
PHUNG, Ngoc-Lam; MARTI, Nicolas; BLANCHE, Antoine; RANC, Nicolas; FAVIER, Véronique; CHRYSOCHOOS, André; SAINTIER, Nicolas; GREGORI, Fabienne; BACROIX, Brigitte; THOQUENNE, Guillaume (Elsevier, 2013)The DISFAT project is a French project financially supported by the French National Agency for Research (ANR). It aims at a deeper understanding of mechanisms leading to crack initiation in metals and alloys under Very ...