Effect of thermal oxidation on the self-assembly of triblock terpolymers
TypeArticles dans des revues avec comité de lecture
This paper reports an investigation of the thermal degradation of a poly(styrene-b-butadiene-b-methyl methacrylate) triblock terpolymer compared with those of butadiene rubbers and poly(styrene-b-methyl methacrylate). According to sol-gel properties changes, it was proposed that polybutadiene blocks undergo mainly crosslinking. However, these latter coexist with chain scissions occurring in polybutadiene blocks, which generates poly(butadiene-b-methyl methacrylate) and poly(butadiene-b-styrene) diblock chains, and possibly chain scissions occurring in polystyrene and poly(methyl methacylate) blocks. The consequences of the degradation on the self-assembly of triblock terpolymer were studied through the annealing kinetics monitored by Atomic Force Microscopy. It appears that at low conversion degrees, chain scissions induce a faster self-assembly kinetics. At higher oxidation degrees, crosslinking of butadiene phase combined with scissions induces a “frozen” state at high annealing times characterized by a macrophase separation.
Showing items related by title, author, creator and subject.
From equilibrium lamellae to out-of-equilibrium cylinders in triblock copolymer nanolayers obtained via multilayer coextrusion MONTANA, Juan-Sebastian; ROLAND, Sébastien; RICHAUD, Emmanuel; MIQUELARD-GARNIER, Guillaume (Elsevier, 2018)Multilayer coextrusion was used to obtain nanolayered films of self-assembled commercial triblock copolymer poly(methyl methacrylate-b-butyl acrylate-b-methyl methacrylate) (MAM) confined by poly(methyl methacrylate) (PMMA). ...
Nanostructuration effect on the mechanical properties of PMMA toughened by a triblock acrylate copolymer using multilayer coextrusion MONTANA, Juan-Sebastian; MIQUELARD-GARNIER, Guillaume; RICHAUD, Emmanuel; ROLAND, SEBASTIEN (Elsevier, 2018)Multilayer coextrusion was used to obtain nanolayered films of self-assembled commercial triblock copolymer poly(methyl methacrylate-b-butyl acrylate-b-methyl methacrylate) (MAM) confined by poly (methyl methacrylate) ...
BIRONEAU, Adrien; DIRRENBERGER, Justin; SOLLOGOUB, Cyrille; MIQUELARD-GARNIER, Guillaume; ROLAND, Sébastien (Wiley, 2016)The size of representative microstructural samples obtained from atomic force microscopy is addressed in this paper. The case of an archetypal one-dimensional nanolayered polymer blend is considered. Image analysis is ...
RICHAUD, Emmanuel; ARRIETA, Juan Sebastian; FAYOLLE, Bruno; NIZEYIMANA, Fidèle (Elsevier, 2016)The thermal oxidative ageing of vinyl ester and unsaturated polyester was studied at temperatures ranging from 120 to 160°C and oxygen pressures ranging from 0.02 to 2.0 MPa. The oxidation of both materials was shown to ...
Dispersion of carbon nanotubes in polypropylene via multilayer coextrusion: Influence on the mechanical properties MIQUELARD-GARNIER, Guillaume; GUINAULT, Alain; FROMONTEIL, D; DELALANDE, S; SOLLOGOUB, Cyrille (ELSEVIER, 2013)Multilayer coextrusion was used to disperse Carbon Nanotubes (CNT) in polypropylene (PP). The dilution of commercially available masterbatches using a twin-screw extruder was first applied to produce several formulations, ...