Flash temperature measurement during dry friction process at high sliding speed
TypeArticles dans des revues avec comité de lecture
An experimental method is presented in this paper to measure flash temperatures of sliding surfaces. High sliding velocities are reached by using a ballistic set-up equipped with a high speed camera. The temperature field on the friction surface was recorded during the process. Tests were conducted under dry sliding conditions by using an identical material for the rubbing bodies, which are of middle hard steel (C22). Experiments showed that the temperature distribution generated by frictional heating is made up of small hot spots that correspond to the friction of asperities located on the sliding surface during very short time. Deduced from observations, maximum local surface temperatures can exceed about 1100 °C around an area less than 100 μm in diameter.
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Experimental studies of Portevin-Le Chatelier plastic instabilities in carbon-manganese steels by infrared pyrometry RANC, Nicolas; DU, W; RANC, I; WAGNER, D (ELSEVIER, 2016)The dynamic strain aging (DSA) phenomenon that occurs in some materials under certain temperature and strain rate conditions can cause plastic strain localization in the form of Portevin-Le Chatelier (PLC) bands. ...
PHUNG, Ngoc-Lam; MARTI, Nicolas; BLANCHE, Antoine; RANC, Nicolas; FAVIER, Véronique; CHRYSOCHOOS, André; SAINTIER, Nicolas; GREGORI, Fabienne; BACROIX, Brigitte; THOQUENNE, Guillaume (Elsevier, 2013)The DISFAT project is a French project financially supported by the French National Agency for Research (ANR). It aims at a deeper understanding of mechanisms leading to crack initiation in metals and alloys under Very ...
About the effect of plastic dissipation in heat at the crack tip on the stress intensity factor under cyclic loading RANC, Nicolas; PALIN-LUC, Thierry; PARIS, Paul C.; SAINTIER, Nicolas (Elsevier, 2013)Because of the reverse cyclic plastic zone at the crack tip, there is plastic dissipation in heat at the crack tip under cyclic loading. That creates a heterogeneous temperature field around the crack tip. A thermo-mechanical ...
About the effect of plastic dissipation in heat at the crack tip on the stress intensity factor under cyclic loading RANC, Nicolas; PALIN-LUC, Thierry; PARIS, Paul.C.; SAINTIER, Nicolas (ELSEVIER, 2014)Because of the reverse cyclic plastic zone at the crack tip, there is plastic dissipation in heat at the crack tip under cyclic loading. That creates a heterogeneous temperature field around the crack tip. A thermomechanical ...
In situ synchrotron ultrasonic fatigue testing device for 3D characterisation of internal crack initiation and growth MESSAGER, Alexandre; JUNET, Arnaud; PALIN-LUC, Thierry; BUFFIÉRE, Jean Yves; SAINTIER, Nicolas; RANC, Nicolas; EL MAY, Mohamed; GAILLARD, Yves; KING, Andrew; BONNIN, Anne; NADOT, Yves (2020)This work presents a new ultrasonic fatigue testing device for studying the initiation and propagation mechanisms of internal microstructurally short fatigue cracks using in situ synchrotron tomography. Its principle is ...