Optimization and comparison of porosity rate measurement methods of Selective Laser Melted metallic parts
Article dans une revue avec comité de lecture
The systematic occurrence of porosities inside selective laser melted (SLM) parts is a well-known phenomenon. In order to improve the density of SLM parts, it is important not only to assess the physical origin of the different types of porosities, but also to be able to measure as precisely as possible the porosity rate so that one may select the optimum manufacturing parameters. Considering 316 L steel parts built with different input energies, the current paper aims to (1) present the different types of porosities generated by SLM and their origins, (2) compare different methods for measuring parts density and (3) propose optimal procedures. After a preliminary optimization step, three methods were used for quantifying porosity rate: the Archimedes method, the helium pycnometry and micrographic observations. The Archimedes method shows that results depend on the nature and temperature of the fluid, but also on the sample volume and its surface roughness. During the micrographic observations, it has been shown that the results depend on the magnification used and the number of micrographs considered. A comparison of the three methods showed that the optimized Archimedes method and the helium pycnometry technique gave similar results, whereas optimized micrographic observations systematically underestimated the porosity rate. In a second step, samples were analyzed to illustrate the physical phenomena involved in the generation of porosities. It was confirmed that: (1) low Volume Energy Density (VED) causes non-spherical porosities due to insufficient fusion, (2) in intermediary VED the small amount of remaining blowhole porosities come from gas occlusion in the melt-pool and (3) in excessive VED, cavities are formed due to the key-hole welding mode.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Texture control of 316L parts by modulation of the melt pool morphology in selective laser melting Article dans une revue avec comité de lectureANDREAU, Olivier; KOUTIRI, Imade; PEYRE, Patrice; PENOT, Jean-Daniel; SAINTIER, Nicolas; PESSARD, Etienne; DE TERRIS, Thibaut; DUPUY, Corinne; BAUDIN, Thierry (Elsevier, 2019)In this study, 316L parts were fabricated with the selective laser melting additive layer manufacturing process using unidirectional laser scan to control their texture. The melt pool shape, microstructure and texture of ...
A competition between the contour and hatching zones on the high cycle fatigue behaviour of a 316L stainless steel: Analyzed using X-ray computed tomography Article dans une revue avec comité de lectureANDREAU, Olivier; PESSARD, Etienne; KOUTIRI, Imade; PENOT, Jean-Daniel; DUPUY, Corinne; SAINTIER, Nicolas; PEYRE, Patrice (Elsevier, 2019)Metal powder bed fusion techniques can be used to build parts with complex internal and external geometries.Process parameters are optimized in order to obtain parts with low surface roughness and porosity, while maintaining ...
Influence of SLM process parameters on the surface finish, porosity rate and fatigue behavior of as-built Inconel 625 parts Article dans une revue avec comité de lectureKOUTIRI, Imade; PESSARD, Etienne; PEYRE, Patrice; AMLOU, Ouafae; DE TERRIS, Thibaut (Elsevier, 2018)This paper is dedicated to understanding fatigue crack initiation for an Inconel 625 manufactured by SLM, using a hatching + contour procedure. In the first part of the paper, an optimum set of parameters was found to ...
Article dans une revue avec comité de lectureSOW, M.C.; DE TERRIS, Thibaut; CASTELNAU, Olivier; HADJEM-HAMOUCHE, Zehoua; COSTE, Frédéric; FABBRO, R.; PEYRE, Patrice (Elsevier, 2020)The use of large beams in the Laser Powder Bed Fusion (L-PBF) process has been receiving increasing attention for the past few years and may widen the dissemination of this technology in the industry, as well as help ...
Influence of the position and size of various deterministic defects on the high cycle fatigue resistance of a 316L steel manufactured by laser powder bed fusion Article dans une revue avec comité de lectureANDREAU, Olivier; PESSARD, Etienne; KOUTIRI, Imade; PEYRE, Patrice; SAINTIER, Nicolas (Elsevier, 2021)Optimized 316L steel samples were manufactured using laser powder bed fusion and tested in high cycle fatigue at R = 0.1. They showed microstructural crack initiation and outstanding fatigue properties. Additional fatigue ...