Rheokinetic of polyurethane crosslinking time-temperature-transformation diagram for rotational molding
TypeArticles dans des revues avec comité de lecture
In this work, the rheokinetic of polyurethane crosslinking was studied by different methods: differential scanning calorimetric (DSC), rheometry, and infrared spectrometry. The conversion ratio and the glass transition temperature were followed by time of reaction. The results of the isothermal and nonisothermal test were compared. The evolution of viscosity was measured at different frequencies. The intersection of these curves is considered as gel point. A simplified mechanism has been proposed for crosslinking reactions. Based on this mechanism, a kinetic model describing the evolution of reactive system was developed. This model then was compared with the results of experiments performed by infrared spectrometry. The time-temperature- transformation diagram was established showing the evolution of physical state change of the reactive system. This diagram may be used to evaluate the zone of rotomoldability of the reactive polyurethane.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
RIVIERE, Sylvain; KHELLADI, Sofiane; FARZANEH, Sedigheh; BAKIR, Farid; TCHARKHTCHI, Abbas (Wiley, 2013)Reactive rotational molding (RRM) is a process to manufacture hollow plastic articles. Comparing to rotational molding of thermoplastics, it decreases the process cycle time due to the reactivity of the system. However, ...
ABDALLAH-ELHIRTSI, Sofiane; FITOUSSI, Joseph; RASHMI, Baralu-Jagannatha; PRASHANTHA, Kalappa; FARZANEH, Sedigheh; LACRAMPE, Marie-France; KRAWCZAK, Patricia; TCHARKHTCHI, Abbas (Wiley Online Library, 2015)In this work, an experimental investigation on a partial shape memory polymer (PSMP) which is transformed into shape memory material is presented. Multicycle shape memory tests are performed on thermoplastic polyurethane ...
TCHARKHTCHI, Abbas; ABDALLAH-ELHIRTSI, Sofiane; EBRAHIMI, Kambiz; FITOUSSI, Joseph; SHIRINBAYAN, Mohammadali; FARZANEH, Sedigheh (MDPI, 2014)In this study some new concepts regarding certain aspects related to shape memory polymers are presented. A blend of polylactic acid (PLA) (80%) and polybutylene succinate (PBS) (20%) was prepared first by extrusion, then ...
TCHARKHTCHI, Abbas; FARZANEH, Sedigheh; ABDALLAH-ELHIRTSI, Sofiane; ESMAEILLOU, Bardia; NONY, Fabien; BARON, A (Taylor & Francis Online, 2014)This study concerns the effect of thermal aging on mechanical properties of polyurethane. Polyurethane samples were exposed at 85° and 120°C under inert atmosphere. Mechanical tests were carried out on these samples the ...
FARZANEH, Sedigheh; FITOUSSI, Joseph; LUCAS, Albert; BOCQUET, Michel; TCHARKHTCHI, Abbas (Wiley, 2013)The relationship between shape and properties memory effect, especially viscoelastic properties of polyurethane under study is the main aim of this research work. Tensile tests have been performed in order to introduce ...