Ring tests on high density polyethylene: Full investigation assisted by finite element modeling
TypeArticles dans des revues avec comité de lecture
In order to characterize the mechanical behavior of HDPE pipes, the ASTM D 2290-04 standard recommends carrying out tensile tests on notched rings, cut out from the pipe. This very simple test is also utilized to investigate the aging effect of the pipe by determining the strain at failure. Comparison between full ring and notched ring mechanical responses are discussed. Constitutive modeling including strain rate effects was performed by finite element analysis. This allowed a better understanding of the stress state in the cross section perpendicular to the loading direction. Additionally, the influence of a thin layer of oxidized HDPE in the inner wall of the ring was studied in the light of the finite element results.
Showing items related by title, author, creator and subject.
DEVILLIERS, Clémence; FAYOLLE, Bruno; LAIARINANDRASANA, Lucien; OBERTI, Sandrine; GAUDICHET-MAURIN, Emmanuelle (Elsevier, 2011)The presence of chlorine in drinking water supplies in many countries creates the undesirable side effect of causing a relatively under investigated degree of polymer degradation in the polyethylene pipes used for transport. ...
Microstructure-mechanical properties relationships in vibration welded glass-fiber-reinforced polyamide 66: A high-resolution X-ray microtomography study MOFAKHAMI, Eeva; TENCÉ-GIRAULT, Sylvie; PERRIN, Jonathan; SCHEEL, Mario; GERVAT, Laurent; OVALLE RODAS, Cristian; LAIARINANDRASANA, Lucien; FAYOLLE, Bruno; MIQUELARD-GARNIER, Guillaume (ELSEVIER, 2020)The effect of initial fiber orientation and welding conditions on the mechanical properties and microstructure of 30 wt% glass-fiber-reinforced polyamide 66 was systematically evaluated. For all conditions studied no ...
CHEMINGUI, Mahmoud; FAYOLLE, Bruno; VERDU, Jacques; FEROUANI, Abdel Karim; LEFEBVRE, Jean–Marc Marc R. (ELSEVIER, 2011)Ageing of polymers results from structural modifications at the molecular scale and kinetic modelling must be elaborated from analysis of the phenomenon at this scale. However, the change of mechanical properties results ...
GOUATY, Gilles; FANG, Lincong; MICHELUCCI, Dominique; DANIEL, Marc; PERNOT, Jean-Philippe; RAFFIN, Romain; LANQUETIN, Sandrine; NEVEU, Marc (Elsevier, 2016)CAD modelers enable designers to construct complex 3D shapes with high-level B-Rep operators. This avoids the burden of low level geometric manipulations. However a gap still exists between the shape that the designers ...
On the role of the spherulitic microstructure in fatigue damage of pure polymer and glass-fiber reinforced semi-crystalline polyamide 6.6 RAPHAEL, Ilan; SAINTIER, Nicolas; ROBERT, Gilles; BEGA, Jéremy; LAIARINANDRASANA, Lucien (ELSEVIER, 2019)Understanding fatigue damage mechanisms in short fiber reinforced thermoplastics is a key issue in order to optimize material processing and propose physically based multiscale fatigue damage models. The present work aims ...