Thermal oxidation of clay-nanoreinforced polypropylene
Type
Articles dans des revues avec comité de lectureAuteur
Date
2010Journal
Polymer Degradation and StabilityRésumé
The thermo-oxidation process at low temperatures for a montmorillonite- nanoreinforced polypropylene (PP) was studied. Experimental aging kinetic data at 100, 80 and 60 °C have been obtained and compared with a computational simulation in which a kinetic model based on the closed loop approach was used. As a result, it has been found that the montmorillonite role is not limited to a role of inert filler in the polymer matrix but induces a slight catalytic effect leading to induction period reduction. This effect has been well simulated by increasing initial hydroperoxyde concentration. The consequences of kinetic control by oxygen diffusion have also been investigated by using micro ATR-FTIR mapping to assess concentration profiles of the oxidation products across the sample thickness. It has been found that the oxidized layer thickness is close to 17 μm for the pure polypropylene whereas it is around 10 μm for the nanocomposite at 100 °C. These profile variations have been attributed to differences in oxygen diffusion coefficient values. Simulations based on the kinetic model including diffusion-reaction coupling describe these profiles well.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
CHOUPIN, Tanguy; FAYOLLE, Bruno; REGNIER, Gilles; PARIS, C.; CINQUIN, Jacques; BRULÉ, Benoît (Elsevier, 2017)Isothermal melt and cold crystallizations of a poly(etherketoneketone) (PEKK) copolymer prepared from diphenyl ether (DPE), terephthalic acid (T) and isophthalic acid (I) with a T/I ratio of 60/40 have been investigated ...
-
CHOUPIN, Tanguy; FAYOLLE, Bruno; RÉGNIER, Gilles; PARIS, Christophe; CINQUIN, Jacques; BRULÉ, Benoît (Elsevier Ltd, 2018)To quantify the isothermal crystallization kinetics of poly(ether ketone ketone) (PEKK), the integration of the crystallization peak measured using differential scanning calorimetry is rendered difficult due to the thermal ...
-
CHOUPIN, Tanguy; BRULE, Benoît; CINQUIN, Jacques; REGNIER, Gilles; FAYOLLE, BRUNO (elsevier, 2018)Macromolecular modifications of poly(etherketoneketone) (PEKK) copolymer prepared from diphenyl ether (DPE), terephthalic acid (T) and isophthalic acid (I) with a T/I ratio of 60/40 have been investigated above its melting ...
-
DEBERTRAND, Louis; FAYOLLE, Bruno; RÉGNIER, Gilles; PARIS, Christophe; CINQUIN, Jacques; BRULÉ, Benoît (Wiley, 2019)Since poly(ether ketone ketone) (PEKK) is a good candidate as a matrix for composite structural parts, the mechanical properties of PEKK copolymers prepared from diphenyl ether, terephthalic acid (T), and isophthalic acid ...
-
GOMEZ ECHEVERRI, Juan Camilo; GODOT, Xavier; DAILLE-LEFEVRE, Bruno; MORALES ARISTIZABAL, Jorge Humberto; MARTIN, Patrick (2020)Des sauts technologiques significatifs sont induits par la mise en oeuvre de l’usine du futur, les interactions entre l’Homme et les équipements de production sont modifiées afin de répondre aux objectifs de réactivité, ...