Diffusion-controlled radiochemical oxidation of bisphenol A polysulfone
Article dans une revue avec comité de lecture
The radiochemical degradation of bisphenol A polysulfone was investigated under a γ-ray dose rate of 24 kGy h-1 up to 30.7 MGy total absorbed dose at 60 °C using gel permeation chromatography, sol-gel analysis, glass transition and rheometry measurements, and oxidation profile measurements by microscopy coupled with Fourier transform infrared analysis in attenuated total reflectance mode. Thin (200 μm) and thick (2 mm) samples were compared. Thin samples undergo mainly chain scissions whereas thick ones undergo mainly crosslinking. The thickness of oxidized layers and, radiochemical yields for chain scissions, crosslinking, oxygen absorption and radical formation were tentatively determined from experimental data in order to determine the influence of oxidative processes on radiochemical ageing and to establish the nature of the crosslinking reactions.
Showing items related by title, author, creator and subject.
Article dans une revue avec comité de lectureRICHAUD, Emmanuel; FERREIRA, Paulo; AUDOUIN, Ludmila; COLIN, Xavier; VERDU, Jacques; MONCHY-LEROY, Carole (Elsevier, 2010)Thin (60 μm) and thick (250 μm) samples of poly(ether ether ketone) were subjected to radiochemical ageing at 24 kGy h -1 dose rate for doses up to 30.7 MGy at 60 °C in air. FTIR spectrophotometry (hydroxyl and carbonyl ...
Article dans une revue avec comité de lectureCOLIN, Xavier; RICHAUD, Emmanuel; VERDU, Jacques; MONCHY-LEROY, Carole (Elsevier, 2010)A non-empirical kinetic model has been built for describing the general trends of radiooxidation kinetics of ethylene-propylene copolymers (EPR) at low γ dose rate and low temperature. It is derived from a radical chain ...
Article dans une revue avec comité de lectureCOLIN, Xavier; MONCHY-LEROY, Carole; VERDU, Jacques (Elsevier, 2011)Three high density polyethylene (PE) samples of different origins, with weight average molar masses ranging from 38 to 63kgmol-1 and displaying a semi-ductile behavior with strain at break εR values of the order of 100-140%, ...
Article dans une revue avec comité de lectureAUDOUIN, Ludmila; COLIN, Xavier; FAYOLLE, Bruno; RICHAUD, Emmanuel; VERDU, Jacques (EDP Sciences, 2010)It has been supposed, for a long time, that kinetic modelling of polymer ageing for nonempirical lifetime prediction was out of reach for two main reasons: hypercomplexity of mechanisms and heterogeneity of reactions. The ...
Chapitre d'ouvrage scientifiqueRICHAUD, Emmanuel; AUDOUIN, Ludmila; COLIN, Xavier; FAYOLLE, BRUNO; VERDU, Jacques (In Tech, 2012)Polymers having an aromatic backbone polymers have a high mechanical strength and a high modulus. Their aromaticity increases their resistance for use in relatively severe conditions especially in aerospace and nuclear ...