Thermal oxidative stability of polyanilines
Article dans une revue avec comité de lecture
Auteur
TRÂN, Thanh HiềnDEBARNOT, Dominique 
RICHAUD, EmmanuelRésumé
This paper deals with thermal ageing of polyaniline obtained from plasma or chemical ways. FTIR analyses suggest the formation of stable carbonyl compounds in both cases. The plasma polyaniline degrades clearly faster than its chemical analog which is discussed from structural considerations. The consequences of thermal ageing on the surface properties monitored by Water Contact Angles (WCA) are also considered and explained as the overlap of an “oxidation” component that decreases WCA and a “crosslinking” component (only observed in plasma polyaniline) responsible for the WCA increase.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lecture; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ;RICHAUD, Emmanuel (Elsevier, 2021)
The need for personal protective equipment increased exponentially in response to the Covid-19 pandemic. To cope with the mask shortage during springtime 2020, a French consortium was created to find ways to reuse medical ...
-
Article dans une revue avec comité de lecture; ;FAYOLLE, Bruno; RICHAUD, Emmanuel (Elsevier, 2016)
The thermal oxidative ageing of vinyl ester and unsaturated polyester was studied at temperatures ranging from 120 to 160°C and oxygen pressures ranging from 0.02 to 2.0 MPa. The oxidation of both materials was shown to ...
-
Article dans une revue avec comité de lecture; ; ; ; ; ;RICHAUD, Emmanuel (Elsevier, 2017)
The in situ thermal oxidation of thin unstabilized polydicyclopentadiene was studied by TGA to monitor mass gain, and DSC to characterize hydroperoxides concentration. Results were discussed using kinetic analysis, which ...
-
Article dans une revue avec comité de lecture;FAYOLLE, Bruno; RICHAUD, Emmanuel (Elsevier, 2017)
Thermal oxidation of three epoxy resins differing by the nature of prepolymer (bisphenol A diglycidyl ether and 1,4-butanediol diglycidyl ether) and hardener (isophorone diamine and 4,7,10-Trioxa-1,13-tridecanediamine) was ...
-
Article dans une revue avec comité de lecture; ; ; ; ; ;RICHAUD, Emmanuel (Elsevier, 2015)
This work aims to determine and understand the influence of UV weathering on the reprocessing of a wood-plastic composite (WPC), i.e. of a wood flour reinforced polypropylene (PP) composites. Two wood flour contents (10% ...