Article dans une revue avec comité de lecture(2013)Indium oxide thin films were grown by the pulsed electron beam deposition method on c-cut sapphire substrates at 10−2 mbar oxygen pressure and temperature up to 500 1C. Such conditions lead to the formation of dense, smooth ...
-
Article dans une revue avec comité de lecture(Wiley, 2013)The morphology and miscibility of commercial poly(lactide) (PLA)/poly(b-hydroxybutyrate) (PHB, from 5 to 20 wt %) blends prepared by melt extrusion method, were investigated using differential scanning calorimetry (DSC) ...
-
Article dans une revue avec comité de lecture(Elsevier, 2013)At high loading rates, the development of adiabatic shear bands in metals is conventionally attributed to the strong interactions induced by viscoplastic dissipation within the bands and thermal softening effects. The ...
-
Article dans une revue avec comité de lecture(IOP Publishing, 2014)The propagation of laser-induced shock waves in a transparent epoxy sample is investigated by optical shadowgraphy. The shock waves are generated by a focused laser (3 ns pulse duration—1.2 to 3.4TWcm−2) producing pressure ...
-
Article dans une revue avec comité de lecture(Wiley, 2013)Several carbon-black filled styrene-butadiene rubbers are subjected to monotonic uniaxial tension tests in order to investi-gate the effects of the amount of fillers and of the crosslink density on their mechanical properties. ...
-
Article dans une revue avec comité de lecture(Elsevier, 2014)The thermo-oxidative degradation of polylactide (PLA) films was studied between 70 and 150 C. It was shown that the oxidative degradation of PLA leads to a random chain cission responsible for a reduction of the molar ...
-
Article dans une revue avec comité de lecture(Wiley-Blackwell, 2013)The decomposition of azodicarbonamide, used as foaming agent in PVC - plasticizer (1/1) plastisols was studied by DSC. Nineteen different plasticizers, all belonging to the ester family, two being polymeric (polyadipates), ...