PBT plasticity loss induced by oxidative and hydrolysis ageing
TypeArticles dans des revues avec comité de lecture
This paper reports the study of embrittlement of PBT submitted either to thermal or hydrolytic ageing. All changes were followed up by tensile tests, rheometry in molten state and gel permeation chromatography for molar mass changes, SAXS and DSC experiments for crystallinity changes. Both kind of ageing were shown to induce predominant chain scissions with moderate crystallinity increase, in great part due to annealing. The combination of all results were used to establish a Mw - χc embrittlement window helping for a determination of an end of life criterion.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
DEFAUCHY, Virginie; LE GAC, Pierre Yves; GUINAULT, Alain; VERDU, Jacques; RECHER, Gilles; DROZDZAK, Renata; RICHAUD, Emmanuel (Elsevier, 2017)The in situ thermal oxidation of thin unstabilized polydicyclopentadiene was studied by TGA to monitor mass gain, and DSC to characterize hydroperoxides concentration. Results were discussed using kinetic analysis, which ...
HUANG, Jing; MINNE, Wendy; DROZDZAK, Renata; RECHER, Gilles; LE GAC, Pierre Yves; RICHAUD, Emmanuel (ELSEVIER, 2020)Thin unstabilized PDCPD film were thermally oxidized in ovens at several temperatures ranging from 50 °C to 120 °C. Hydroperoxide concentration was monitored by DSC. It was observed that hydroperoxides concentration reaches ...
HUANG, Jing; RICHAUD, Emmanuel; LE GAC, Pierre-Yves; DAVID, Adelina; DROZDZAK, Renata; GILLES, Recher (Elsevier, 2020)Polydicyclopentadiene (PDCPD) is a thermoset polymer synthetized from Ring Opening Metathesis Polymerization and produced by Reaction Injection Moulding process. Due to its interesting properties, like short processing ...
DIANI, Julie; FREDY, Carole; GILORMINI, Pierre; MERCKEL, Yannick; REGNIER, Gilles; ROUSSEAU, Ingrid (Elsevier, 2011)A torsion device was designed and built for testing the shape fixity and shape recovery of shape memory polymers at large deformation. A simple thermal chamber was used to regulate the thermal environment during testing ...
Influence of thermal diffusion and shear-thinning during the leveling of nanoimprinted patterns in a polystyrene thin film TEYSSEDRE, Hubert; LANDIS, Stefan; GILORMINI, Pierre; REGNIER, Gilles (Springer, 2015)When capillary forces prevail, the leveling of the free surface of a fluid film is a natural phenomenon that has already found applicative interest either with brushmarks for paint coatings or for rheology on polymeric ...