A new analytical model for predicting the radio-thermal oxidation kinetics and the lifetime of electric cable insulation in nuclear power plants. application to silane cross-linked polyethylene
Article dans une revue avec comité de lecture
The radio-thermal oxidation of silane cross-linked polyethylene (Si-XLPE) was studied in air under different γ dose rates (6.0, 8.5, 77.8, and 400 Gy.h−1) at different temperatures (21, 47, and 86°C). The changes in the physico-chemical and mechanical properties of Si-XLPE throughout its exposure were determined by FTIR spectroscopy, differential scanning calorimetry (DSC), swelling measurements, rheometry in rubbery (DMTA) and in molten states, and uniaxial tensile testing. It was found that oxidation leads to the build-up of a wide variety of carbonyl and hydroxyl products (mostly carboxylic acids and hydroperoxides) and an efficient chain scission process that catastrophically reduces the concentration in elastically active chains and the elongation at break from the early periods of exposure. A new analytical model was derived from the current radio-thermal mechanistic scheme without making the usual assumption of thermal stability of hydroperoxides. After an initial period where the oxidation kinetics occurs with a constant rate, this model allows also predicting the auto-acceleration of the oxidation kinetics when the hydroperoxide concentration reaches a critical value of about 1.6 × 10−1 mol.L−1. Choosing this critical value as a structural end-of-life criterion allows a more direct assessment of the lifetime of Si-XLPE in the various radio-thermal environments under study, except at the highest temperature (i.e. 86°C) where the kinetic model can still be noticeably improved.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Physico-chemical characterization of the blooming of Irganox 1076® antioxidant onto the surface of a silane-crosslinked polyethylene Article dans une revue avec comité de lectureThis study aims at investigating the blooming of Irganox 1076® onto the surface of a silane-crosslinked polyethylene. Preliminary studies on the commercial Irganox 1076® powder enabled to identify its crystalline structure ...
Ageing Assessment of XLPE LV Cables for Nuclear Applications through Physico-Chemical and Electrical Measurements Article dans une revue avec comité de lectureThis paper investigates the changes in electrical and physico-chemical properties of low-voltage power cables for nuclear application when subjected to the combined effects of gamma radiation and temperature. Electrical ...
Thermal ageing of a silane-crosslinked polyethylene stabilised with a thiodipropionate antioxidant Article dans une revue avec comité de lecturehe thermal ageing of a silane-crosslinked polyethylene stabilised with 1 wt% of distearyl thiodipropionate (Irganox PS802) was studied in air at three different temperatures: 87 °C, 110 °C, and 130 °C. FTIR spectroscopy ...
Article dans une revue avec comité de lectureThis work focuses on the thermal ageing in air of a silane-crosslinked polyethylene stabilised with an excess of phenolic antioxidant (Irganox 1076®) in the temperature range between 87°C and 130°C. In such case, it was ...
Multi scale aging assessment of low-voltage cables subjected to radio-chemical aging: Towards an electrical diagnostic technique Article dans une revue avec comité de lectureIn this article, the aging behavior of nuclear-grade low voltage cables, characterized by different geometries and insulation compositions, is investigated. Cables were subjected to radio-chemical aging at different dose ...