Microstructure investigation of hydrothermal damage of aged SMC composites using Micro-computed tomography and scanning electron microscopy
TypeArticles dans des revues avec comité de lecture
This paper presents an investigation on the effects of hydrothermal aging on Sheet Molding Compound (SMC) composite. Two different techniques were carried out to study the inner structure of aged SMC composite. Firstly, X-ray micro computed tomography (XµCT) was used to evaluate the changes using 3D images. The results showed cracks in all the composite structure with different shapes and volume in response to the hydrothermal conditions. The cracks results from the build up of an osmotic pressure in microcavities, which is proportional to water concentration. However, it was not possible to quantify separately the hydrothermal induced damage in the studied SMC composite material. Therefore, the XµCT analyzes were supplemented by a microscopic study. This step has been studied in terms of crack density evolution and crack propagation rate. The results obtained by XµCT technique and SEM observations show that the damage increases continuously with time and temperature during aging. The damage was found to be located in the voids contained in the matrix at early stage of aging. Then it is mostly developed into the fiber interface in the form of fiber/matrix interfacial debonding.
Files in this item
Showing items related by title, author, creator and subject.
Microstructure investigation of hydrothermal damage of aged SMC composites using Micro-computed tomography and scanning electron microscopy ABDESSALEM, Abir; TAMBOURA, Sahbi; FITOUSSI, Joseph; DALY, Hachmi Ben; TCHARKHTCHI, Abbas; MERAGHNI, Fodil (Elsevier BV, 2021)This paper presents an investigation on the effects of hydrothermal aging on Sheet Molding Compound (SMC) composite. Two different techniques were carried out to study the inner structure of aged SMC composite. Firstly, ...
ABDESSALEM, Abir; TAMBOURA, Sahbi; FITOUSSI, JOSEPH; BEN DALY, Hachmi; TCHARKHTCHI, Abbas (Wiley, 2020)Sheet molding compound (SMC) composite has been studied under humid-aging conditions. Diffusion of water within the material, as measured by gravimetry, was found to be in good agreement with the “Langmuir-type” diffusion ...
Fast fatigue life prediction of short fiber reinforced composites using a new hybrid damage approach: Application to SMC LARIBI, M.A.; TAMBOURA, Sahbi; FITOUSSI, JOSEPH; TCHARKHTCHI, Abbas; BEN DALI, H. (2018)Industrial design of Short Fiber Reinforced Composites (SFRC) structures is subject to several compounding and processing steps of optimization. Moreover, these structures are often submitted to fatigue loading. Therefore, ...
Experimental and numerical multi-scale approach for Sheet-Molding-Compound composites fatigue prediction based on fiber-matrix interface cyclic damage TAMBOURA, Sahbi; AYARI, H.; SHIRINBAYAN, Mohammadali; LARIBI, M. A.; BENDALY, Hachmi; SIDHOM, Habib; TCHARKHTCHI, Abbas; FITOUSSI, Joseph (ELSEVIER, 2020)In this paper, a multi-scale approach is proposed to predict the stiffness reduction of a Sheet-Molding-Compound (SMC) composite submitted to low cycle fatigue (until 2.105 cycles). Strain-controlled tensile fatigue tests ...
Characterization of a New Fully Recycled Carbon Fiber Reinforced Composite Subjected to High Strain Rate Tension MEFTAH, Hassen; TAMBOURA, Sahbi; FITOUSSI, Joseph; TCHARKHTCHI, Abbas; BENDALY, Hachmi (Springer Netherlands, 2017)The aim of this study is the complete physicochemical characterization and strain rate effect multi-scale analysis of a new fully recycled carbon fiber reinforced composites for automotive crash application. Two composites ...