Mechanical and macromolecular changes during thermal degradation of polyphenylsulfone
Article dans une revue avec comité de lecture
Date
2022-01Journal
Polymer Degradation and StabilityRésumé
Polyphenylsulfone was thermally aged at temperatures corresponding to its processing and was mainly shown to undergo crosslinking as observed by measurements of average molar mass, rheometry and changes in glass transition temperature. Those experiments were completed by mechanical testing thin sample films at 250 and 280 °C. The same degradation mechanisms were observed and result in a strong decrease of ultimate strain accompanied by a slight decrease in elastic modulus and yield stress. Overall results were discussed using well know structure-properties relationships.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lecture
DELANNOY, Romain; QUELENNEC, Blandine;
TOGNETTI, Vincent;
DELBREILH, Laurent;
DELPOUVE, Nicolas;
RICHAUD, Emmanuel (2023)
Four epoxy-amine networks were characterized by Dynamical Mechanical Analysis (DMA) and by Dielectric Relaxation Spectroscopy (DRS). The epoxy-amine networks were cured with DGEBA and four aliphatic amine hardeners: three ... -
Article dans une revue avec comité de lectureDELOZANNE, Justine; MONTANA, Juan Sebastian; GUINAULT, Alain; DESGARDIN, Nancy;
CUVILLIER, Nicolas;
RICHAUD, Emmanuel (Taylor & Francis, 2022-04)
This paper reports the failure of bonded assemblies submitted to thermal ageing. Adhesives are either fully or incompletely cured. Despite comparable initial properties, depletion of mechanical properties (evaluated from ... -
Article dans une revue avec comité de lectureBELLILI, Amar; DAVID, Nicolas; WANG, Qingxiao; GOUTILLE, Yannick;
RICHAUD, Emmanuel (Elsevier, 2012)
This paper reports a study of mineral oil diffusion through a filled ethylene-vinyl acetate crosslinked polymer, together with some comparisons with aliphatic linear hydrocarbons. Permeation was monitored by classical ... -
Article dans une revue avec comité de lectureThe thermal oxidation of DGEBA-DDS (bisphenol A diglycidyl ether + 4,4′-diaminodiphenyl sulfone) and TGMDA-DDS (4,4′-methylenebis(N,N-diglycidylaniline) + 4,4′-diaminodiphenyl sulfone) was performed at 80, 120, and 200 °C ...
-
Article dans une revue avec comité de lectureNICOLAS, Clémence; HUANG, Jing; MINNE, Wendy; DROZDZAK, Renata; RECHER, Gilles; FONTAINE, Laurent; MONTEMBAULT, Véronique;
RICHAUD, Emmanuel (Elsevier, 2021)
A series of new norbornene monomers containing sterically hindered phenol groups have been synthesized and polymerized via ring-opening metathesis polymerization (ROMP) using the Grubbs 3rd generation catalyst (G3’). ROMPs ...