Effects of Process Parameters on Microstructure and Mechanical Properties of Semi-Solid Al-7Si-0.5Mg Aluminum Alloy by Gas Induced Semi-Solid Process
Article dans une revue avec comité de lecture
Auteur
Résumé
Al-7Si-0.5Mg aluminum alloy semi-solid slurry with good spherical grains was prepared by gas induced semi-solid process (GISS) and the effects of both holding time and medium alloy addition on the microstructure of the semi-solid slurry were investigated. These two parameters have a great influence on the solid fraction, the size and the sphericity of the grains. With holding time increased from 85 s to 270 s, the solid phase fraction of the semi-solid slurry decreased from ~0.77 to ~0.67, the average grain size increased from ~95 μm to ~225 μm and the average shape factor decreased from ~0.80 to ~0.33. When medium alloy addition varied in the range of 0.5–2.0 wt%, a better slurry microstructure was obtained at about 1.5 wt%. Compared with the conventional liquid die-casting, the semi-solid die-casting improved the mechanical properties of tensile bars; yield strength, tensile strength and elongation of tensile bars reached ~240 MPa, ~307 MPa and ~8.8% after heat treatment, respectively. In conclusion, GISS process can prepare the semi-solid slurry with uniform and round microstructure, and the semi-solid die-casting can improve mechanical proper ties of Al-7Si-0.5Mg aluminum alloy.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lectureGU, Guo-Chao; XIANG, Li-Xin; LI, Rui-Fen; ZHENG, Hong-Liang; LU, Yu-Peng; PESCI, Raphaël (Elsevier BV, 2023-09)The challenges commonly associated with conventional high pressure die casting (HPDC) have led to increased interest in semi-solid metal (SSM) forming processes. In the present study, semi-solid slurries of A356 alloy ...
-
Conférence invitéeAfter analazing,the microstructure of the thixoforged parts, some mechanisms of material flow are proposed.
-
Article dans une revue avec comité de lectureThe distribution of liquid at the semi solid state is one of the most important parameters for steel thixoforging. It has a great influence on the viscosity of the material, on the flows and finally on the final shape and ...
-
Communication avec acteBECKER, Eric; GU, Guochao; PESCI, Raphaël; LANGLOIS, Laurent (Association Française de Mécanique, 2011)Le comportement d’un alliage mis en forme à l’état semi-solide n’est toujours pas bien compris. Afin d’établir l'influence de différents paramètres sur l'écoulement de la matière, un processus de thixoextrusion expérimental ...
-
Communication avec acteThixoforging, one variant of semi-solid metal processing in which the metallic alloys are processed at low liquid fraction (0.1< Fl < 0.3), is used to produce complex parts with high mechanical properties. Steel thixoforging ...