Volume changes in a filled elastomer studied via digital image correlation
Article dans une revue avec comité de lecture
Auteur
Résumé
Volumetric strains in a filled SBR specimen subjected to cyclic uniaxial tension with increasing extensions are studied. Digital image correlation is used to follow the kinematics of two orthogonal free faces. A volume expansion is observed past a critical elongation, which can be interpreted as the onset of cavitation. Under unloading, the volume returns to its original value and remains constant upon reloading. Increasing the elongation to higher values than the previous cycle leads again to a volumetric expansion.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lectureMERCKEL, Yannick; DIANI, Julie; BRIEU, Mathias; CAILLARD, Julien (Elsevier, 2012)Original constitutive modeling is proposed for filled rubber materials in order to capture the anisotropic softened behavior induced by general non-proportional pre-loading histo-ries. The hyperelastic framework is grounded ...
-
Article dans une revue avec comité de lectureMERCKEL, Yannick; DIANI, Julie; BRIEU, Mathias; CAILLARD, Julien (Wiley, 2013)Several carbon-black filled styrene-butadiene rubbers are subjected to monotonic uniaxial tension tests in order to investi-gate the effects of the amount of fillers and of the crosslink density on their mechanical properties. ...
-
Article dans une revue avec comité de lectureMERCKEL, Yannick; DIANI, Julie; BRIEU, Mathias; GILORMINI, Pierre; CAILLARD, Julien (Wiley, 2012)A quantitative estimate of the Mullins softening is proposed and tested on various carbon-black filled styrene-butadiene rubbers. In order to model the behaviour of elastomeric materials, some constitutive equations reported ...
-
Article dans une revue avec comité de lectureMERCKEL, Yannick; DIANI, Julie; BRIEU, Mathias; GILORMINI, Pierre; CAILLARD, Julien (American Chemical Society, 2011)Several carbon-black filled styrene-butadiene rubbers showed different sensibilities to the Mullins softening when submitted to cyclic uniaxial tension. In order to quantify this softening, a damage parameter was introduced. ...
-
Article dans une revue avec comité de lectureMERCKEL, Yannick; BRIEU, Mathias; DIANI, Julie; CAILLARD, Julien (Elsevier, 2012)Samples of carbon-black filled styrene butadiene rubbers (SBRs) were submitted to successive nonproportional loadings in order to define a general criterion for the Mullins softening. For this purpose, each sample was ...