Structure and molecular dynamics of multilayered polycarbonate/polystyrene films.
Article dans une revue avec comité de lecture
Date
2012Journal
Journal of Applied Polymer ScienceRésumé
Multilayered film polycarbonate/polystyrene (PC/PS) comprising 257 layers with total thickness 125 m was made by coextrusion process. The nominal thickness of PC layers was 680 nm, and the nominal thickness of PS layers was 290 nm. Additionally the control samples of PC and PS with the thickness of 125 m were coextruded in the same way. There was reasonably good correlation between the PC and PS layers real thickness as measured by AFM and the estimated thickness determined from the processing parameters. Significant shift of glass transition temperature is observed in multilayer film: for PS component towards higher temperature while PC still being glassy and for PC towards lower temperature while PS being in rubbery phase. In order to investigate the amplitude and geometry of fast segmental motions, the LG-CP NMR technique under fast magic-angle spinning was used. 2D 13C – 1H LG-CP spectra of PC, PS and PC/PS 70/30 were recorded at various temperatures. Cross sections of aromatic carbons spectra show us the influence of PC on PS and vice versa. It gives us also the information about PS and PC segmental motion as a function of temperature: above the glass transition temperature of PS, the PC component of a multilayer film, although still being in glassy state, becomes more flexible.
Fichier(s) constituant cette publication
- Nom:
- PIMM_JAPS_1_2012-regnier.pdf
- Taille:
- 1.141Mo
- Format:
- Description:
- Article publié
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Article dans une revue avec comité de lectureLY, Haibang; LE, Tien Thinh; LE, Vuongminh; PHAM, Binh Thai;
DAL, Morgan;
REGNIER, Gilles;
MONTEIRO, Eric (MDPI, 2019)
The presence of defects like gas bubble in fabricated parts is inherent in the selective laser sintering process and the prediction of bubble shrinkage dynamics is crucial. In this paper, two artificial intelligence (AI) ... -
Article dans une revue avec comité de lectureA quick evaluation of the forces involved in nanoimprint would be very helpful in the prevention of mold deflection. Unfortunately, it is shown here that assuming simplified flows may lead to quite incorrect evaluations ...
-
Shear-strain step response in linear regime of dilute suspensions of naturally bent carbon nanotubes Article dans une revue avec comité de lectureImpressive enhancements of the storage modulus have been documented when low volume fractions of single wall carbon nanotubes (SWNTs) are added to a Newtonian solvent for obtaining dilute suspensions. The intrinsic bending ...
-
Article dans une revue avec comité de lectureA dual experimental-numerical approach was carried out to estimate thermal cycles and resulting fusion depths obtained during the selective laser sintering (SLS) of two polymers: PA12 and PEKK. The validation of thermal ...
-
Article dans une revue avec comité de lectureKinetic theory is a mathematical framework intended to relate directly the most relevant characteristics of the molecular structure to the rheological behavior of the bulk system. In other words, kinetic theory is a ...