Water clustering in polychloroprene
TypeArticles dans des revues avec comité de lecture
Water sorption has been studied gravimetrically for polychloroprene rubber samples, first at a fixed hygrometric ratio (98% HR) and several temperatures (25, 40, 60 and 80 °C) for samples of 1.8 and 3.8 mm thickness (Constant Temperature and Hygrometry, CTH experiments), then at fixed temperature (40 °C) and several hygrometric ratios ranging from 0 to 95% HR on samples of 0.1 mm thickness (DVS experiments). CTH experiments reveal an abnormal sorption behavior: after an apparently fickian transient period, the water absorption continues at almost constant rate, no equilibrium is observed after more than 2500 h, whatever the temperature. DVS experiments reveal a very low Henry's solubility but the formation of clusters at water activities higher than 40%. The water diffusivity is almost independent of activity below 50% HR and decreases rapidly when activity increases above 50%. Contrary to CTH experiments, equilibrium is reached in DVS and the difference is not simply linked to the well-known effect of sample thickness on diffusion rate. The results allow hypotheses such as hydrolysis or osmotic cracking to explain the abnormal sorption phenomenon to be rejected. It is suggested that clusters could be polymer-water complexes having a linear/branched structure able to grow without phase separation that could explain the reversibility of sorption-desorption cycles. The difference of behavior between thin 0.1 mm and thicker 1.8 or 3.8 mm samples could be due to an effect of swelling stresses.
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Role of strain induced crystallization and oxidative crosslinking in fracture properties of rubbers LE GAC, Pierre Yves; BROUDIN, Morgane; ROUX, Gérard; VERDU, Jacques; DAVIES, Peter; FAYOLLE, Bruno (Elsevier, 2014)Tensile properties and crack propagation properties, especially critical strain energy release rate in mode I, GIC, have been used to investigate fracture properties of elastomers and their relationships with microstructure. ...
LE GAC, Pierre Yves; ROUX, Gérard; VERDU, Jacques; DAVIES, Peter; FAYOLLE, Bruno (Elsevier, 2014)Thermal oxidation in air at atmospheric pressure, in the 80-140 °C temperature range and in oxygen at 100 °C in the 0.02-3 MPa pressure range, of unvulcanized, unstabilized, unfilled polychloroprene (CR) has been characterized ...
LE GAC, Pierre Yves; CELINA, Mathew C.; ROUX, Gérard; VERDU, Jacques; DAVIES, Peter; FAYOLLE, Bruno (Elsevier Ltd, 2016)The oxidative ageing in the range of 60 °C–140 °C of sulfur vulcanized polychloroprene has been studied by FTIR spectroscopy (double bond consumption), modulus changes and oxygen absorption measurements. Experiments were ...
RICHAUD, Emmanuel; LE GAC, Pierre Yves; VERDU, Jacques; LE GAC, Pierre Yves (Elsevier, 2014)Thermal aging of thin ﬁlms of unstabilized polydicyclopentadiene (pDCPD) at several temperatures ranging from 120 to 30 C was investigated by means of carbonyl build up by FTIR with ammonia derivatization, double bond ...
Impact of fillers (short glass fibers and rubber) on the hydrolysis-induced embrittlement of polyamide 6.6 LE GAC, Pierre Yves; FAYOLLE, BRUNO (elsevier, 2018)This study deals with the durability of composites based on polyamide 6.6 (PA6.6) in a humid environment, and more especially, with the loss of fracture properties. It is known that PA6.6 undergoes plasticization in the ...