Plastisol Gelation and Fusion Rheological Aspects
Article dans une revue avec comité de lecture
This study deals with the rheological aspects of poly-vinyl chloride (PVC) plastisol gelation and fusion processes in foamable formulations. Here, such processes are simulated by temperature-programmed experiment (5 K min−1) in which complex viscosity components are continuously recorded. Nineteen samples based on a PVC-VAC (vinyl acetate 95/5) copolymer with 100 phr plasticizer have been studied, differing only by the plasticizer structure. The sample shear modulus increases continuously with temperature until a maximum, long time after the end of the dissolution process as characterized by DSC. The temperature at the maximum varies between 345 and 428 K with a clear tendency to increase almost linearly with the plasticizer molar mass, and to vary with the flexibility and the degree of branching of the plasticizer molecule. The shear modulus increase is interpreted in terms of progressive “welding” of swelled particles by polymer chain reptation. The plasticizer nature would mainly affect the friction parameter of chain diffusion
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Plastisol Foaming Process. Decomposition of the Foaming Agent, Polymer Behavior in the Corresponding Temperature Range and Resulting Foam Properties Article dans une revue avec comité de lectureVERDU, Jacques; ZOLLER, Agnes; MARCILLA, Antonio (Wiley-Blackwell, 2013)The decomposition of azodicarbonamide, used as foaming agent in PVC - plasticizer (1/1) plastisols was studied by DSC. Nineteen different plasticizers, all belonging to the ester family, two being polymeric (polyadipates), ...
Thermo-oxidation behaviour of composite materials at high temperatures: A review of research activities carried out within the COMEDI program Article dans une revue avec comité de lectureLAFARIE, Marie Christine; GRANDIDIER, Jean Claude; OLIVIER, Loic; COLIN, Xavier; VERDU, Jacques; CINQUIN, Jacques (Elsevier, 2010)The present paper presents a review of the main activities carried out within the context of the COMEDI research program, a joint collaboration involving three research teams focusing on the thermo-oxidation behaviour of ...
Article dans une revue avec comité de lectureRICHAUD, Emmanuel; FAYOLLE, Bruno; VERDU, Jacques (Elsevier, 2011)This article deals with polypropylene stabilization by hindered 2,6-di-tert-butylphenols. Two aspects are mainly considered: the influence of stabilizer structure, of its concentration and temperature on induction period ...
Article dans une revue avec comité de lectureRICHAUD, Emmanuel; OKAMBA-DIOGO, Octavie; FAYOLLE, Bruno; VERDU, Jacques; GUILMENT, Jean; FERNAGUT, François (Elsevier, 2013)The literature on oxidation kinetics of polyamides and model compounds has been reviewed in order to try to extract suitable information for non-empirical kinetic modeling. Polyamide characteristics are systematically ...
Article dans une revue avec comité de lectureOKAMBA-DIOGO, Octavie; RICHAUD, Emmanuel; VERDU, Jacques; FERNAGUT, François; GUILMENT, Jean; FAYOLLE, Bruno (Elsevier, 2014)The present article reports a study of thermal oxidation of unstabilized polyamide 11 films at several temperatures (90–165 °C) under atmospheric pressure and under various oxygen pressures (up to 1.6 MPa) at 110 °C. The ...