Platicizer effect on network structure and hydrolytic degradation
TypeArticles dans des revues avec comité de lecture
The hydrolytic degradation of fully cured polyester-urethane networks polymerized in the presence of several weight ratios of triacetin was monitored by the residual concentration in elastically active chains obtained from modulus and equilibrium solvent swelling measurements. The presence of triacetin does not change the water uptake but induces a lower rate of degradation. Comparisons were performed with networks in which triacetin was removed before ageing, and with networks in which polyester-urethane was first polymerized and then impregnated by triacetin. Data suggest that the presence of triacetin during polymerization induces the presence of elastically inactive chains such as dangling chains, loops… the hydrolysis of which does not change the elastic properties of the network. This explanation was checked from relaxation measurements by n.m.r and d.m.a, and by the analysis of the soluble fraction generated by hydrolysis.
Showing items related by title, author, creator and subject.
RICHAUD, Emmanuel; GILORMINI, Pierre; COQUILLAT, Marie; VERDU, Jacques (Wiley, 2014)The hydrolysis of almost ideal networks based on macrodiols of average molar mass about 2 kg mol 1, with L¼18 ester groups per chain is studied. Tensile testing is used to evaluate the crosslink density through the statistical ...
GILORMINI, Pierre; RICHAUD, Emmanuel; VERDU, Jacques (Elsevier, 2017)Methyl methacrylate-ethylene glycol dimethacrylate networks were synthetized and submitted to radiochemical degradation, with ageing monitored by means of sol-gel analysis. The networks were shown to undergo chain scission ...
GILORMINI, Pierre; RICHAUD, Emmanuel; VERDU, Jacques (Elsevier, 2014)A statistical theory was proposed for the degradation (random scission of chains) of a network having f-functional nodes in the case where all chains contain equireactive groups and a chain scission event does not create ...
DELOZANNE, Justine; DESGARDIN, Nancy; CUVILLIER, Nicolas; RICHAUD, Emmanuel (Elsevier Ltd, 2019)The thermal oxidation of DGEBA-DDS (bisphenol A diglycidyl ether + 4,4′-diaminodiphenyl sulfone) and TGMDA-DDS (4,4′-methylenebis(N,N-diglycidylaniline) + 4,4′-diaminodiphenyl sulfone) was performed at 80, 120, and 200 °C ...
A numerical study of the influence of polydispersity on the behaviour until break of a reinforced hyperelastic material with a cohesive interface TOULEMONDE, Paul-Aymé; DIANI, Julie; GILORMINI, Pierre; DESGARDIN, Nancy (EDP Sciences, 2015)Solid propellants manufacturers commonly monitor the granulometries of the explosive fllers they introduce in the material to pack high fller volume fraction and thus obtain satisfactory energetic performance. However, to ...