Effect of nanosilica additive particles on both friction and wear performance of mild steel/CuSn/SnBi multimaterial system
Type
Articles dans des revues avec comité de lectureDate
2015Journal
Tribology InternationalAbstract
This paper presents an experimental study of the tribological behaviour of a multimaterial system using conventional powder metallurgy process with SiO2 nanoparticles. Four configurations were studied with and without SiO2. The tribological properties of the sintered materials were analysed by wear experiments at lubricated conditions on a ball disc wear test rig. The results are compared with those of conventional material for journal bearing. These show less variation of the friction coefficient and less wear rate for the materials with SiO2 compared to the ones without SiO2 and to those of the reference material. The dominant wear mechanism is adhesive wear, accompanied by mild abrasive wear.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
AIT SADI, Hassiba H; BRITAH, M.; HATTALI, L; NECIB, K; IOST, Alain A.; MESRATI, N (Centre pour Ia Communication Scientifique Directe, 2013)L'identification des proprietes tribologiques des materiaux reste encore une voie tres ouverte. En effet, Ia problematique scientifique traitee par les chercheurs de divers laboratoires est centree sur I'experimentation ...
-
AIT SADI, H.; BRITAH, M.; IOST, Alain; MESRATI, N. (Polska Akademia Nauk, 2013)Copper-lead was investigated by scratch tests under two set of experiments conditions: at progressive loads (0 – 200 N) and at two different constant loads (20 – 30 N). These tests were made to assess the adhesion ...
-
AIT SADI, H.; BRITAH, M.; HATTALI, L.; NECIB, K.; IOST, Alain; MESRATI, N (Société Tribologique de France, 2013)L'identification des propriétés tribologiques des matériaux reste encore une voie très ouverte. En effet, Ia problématique scientifique traitée par les chercheurs de divers laboratoires est centrée sur I' expérimentation ...
-
RUELLAN, A; GUINAULT, Alain; SOLLOGOUB, Cyrille; CHOLLET, G; AIT-MADA, A; DUCRUET, Violette; DOMENEK, Sandra (Budapest University of Technology and Economics, 2015)The use of industrial by-products of the vegetable oil industry as ductility increasing additives of polylactide (PLA) was investigated. Vegetable oil deodorization condensates were melt-blended by twin-screw extrusion up ...
-
VAN GORP, Adrien; BIGERELLE, Maxence; GRELLIER, Alain; IOST, Alain; NAJJAR, Denis (ELSEVIER, 2007)This paper proposes a new multi-scale measurement approach performed to compare the surface roughness and the visual aspect of polished surfaces. In this investigation, five specimens of glass moulds presenting different ...