Effect of O2 increase on properties of vanadium oxide coatings
TypeArticles dans des revues avec comité de lecture
The present research was carried out with the aim of studying the influence of oxygen concentration during processing on the properties of the VOx coatings deposited by cathodic magnetron sputtering on a stainless steel AISI 316L substrate. Mechanical and tribological properties were measured by nanoindentation and sliding wear tests respectively. Adhesion was evaluated by means of the scratch test. In order to determine the texture of the coatings, complementary characterization methods including X-ray diffraction in grazing incidence and Bragg Brentano configurations, as well as V scans, were performed. It was found that the texture of the crystalline coatings is strongly influenced by the amount of partial pressure of oxygen in the reactor atmosphere. The V2O5 phase, with an orthorhombic symmetry, was produced in the coating, which had a pronounced texturing for the (001) plane, exhibiting the best values of hardness and Young modulus. It was shown that, as the oxygen concentration drops to ,1 sccm, the mechanical and tribological characteristics, as well as the coating adhesion, tend to decrease considerably.
Files in this item
Showing items related by title, author, creator and subject.
ZAIRI, Amel; NOUVEAU, Corinne; LARBI, Ahmed Beb Cheikh; IOST, Alain; MARTIN, Nicolas; BESNARD, Aurélien (Maney Publishing, 2014)CrSiN films were deposited by reactive radio frequency magnetron sputtering in an Ar+N2 gas mixture. The nitrogen gas was injected in the deposition chamber using two methods: the classical constant injection and pulsed ...
STAIA, Mariana; PUCHI-CABRERA, Eli-Saul; IOST, Alain; ZAIRI, Amel; BELAYER, S.; VAN GORP, Adrien (ELSEVIER, 2015)Considerable improvement in the tribological response was achieved during sliding wear tests against alumina ball, when AA 2024-T3-aluminium alloy substrate was coated with DLC/NiP duplex coating. Quantitative EPMA analysis ...
STAIA, Mariana; TROCELIS, A; ZAIRI, Amel; SUAREZ, M; PUCHI-CABRERA, Eli-Saul; IOST, Alain; MONTAGNE, Alex (2016)The present work has been conducted in order to assess the mechanical and tribological performance of a ZrN coating deposited onto a H13 steel substrate by means of a closed field unbalanced magnetron-sputtering ion-plating ...
FELLAH, Mamoun; AISSANI, Linda; ZAIRI, Amel; ABDUL SAMAD, Mohamed; NOUVEAU, Corinne; TOUHAMI, Mohamed Zine; DJEBAILI, Hamid; MONTAGNE, Alex; IOST, Alain (Informa UK Limited, 2018)In the present study, the effect of thermal treatment on the mechanical and structural properties of chromium carbide coatings with different thicknesses is evaluated. The coatings were deposited by cathodic magnetron ...
Fatigue behavior of a structural steel coated with a WC–10Co–4Cr/Colmonoy 88 deposit by HVOF thermal spraying LA BARBERA-SOSA, J.G.; SANTANA, Y.Y.; VILLALOBOS-GUTIERREZ, C.; CHICOT, Didier; LESAGE, J.; DECOOPMAN, Xavier; IOST, Alain; STAIA, M.H.; PUCHI-CABRERA, Eli-Saul (ELSEVIER, 2013)The fatigue behavior of a SAE 4340 steel, coated with a 50% WC–10Co–4Cr/50% Colmonoy 88 deposit, by high velocity oxygen fuel (HVOF) thermal spray, has been investigated. The change in the maximum alternating stress with ...