Ultrasonic fatigue tests at high temperature on an austenitic steel
TypeArticles dans des revues avec comité de lecture
The objective of this paper is to study the gigacycle fatigue behavior of an austenitic steel at temperatures of 600 °C and 700 °C under fully reverse loading (R=−1). Numerical simulation by finite element method (FEM) was used to design the specimens and to analyze the effects of the variation in the dynamic Young modulus with temperature from measurements of the ultrasonic resonance frequency. Finally, new stress-life curves for this material are presented for a lifetime range from 105 to 109 cycles at room temperature, 600 °C and 700 °C.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Very high cycle fatigue for single phase ductile materials: Comparison between α-iron, copper and α-brass polycrystals FAVIER, Véronique; BLANCHE, Antoine; WANG, Chong; PHUNG, Ngoclam; RANC, Nicolas; WAGNER, Daniele; BATHÌAS, Claude; CHRYSOCHOOS, André; MUGHRABI, Haeel (elsevier, 2016)In this paper, the main results obtained in the framework of a National French Agency project called DISFAT, standing for “Dissipation in Fatigue”, are presented. The project was dedicated to the microplastic mechanisms ...
Experimental studies of Portevin-Le Chatelier plastic instabilities in carbon-manganese steels by infrared pyrometry RANC, Nicolas; DU, W; RANC, I; WAGNER, D (ELSEVIER, 2016)The dynamic strain aging (DSA) phenomenon that occurs in some materials under certain temperature and strain rate conditions can cause plastic strain localization in the form of Portevin-Le Chatelier (PLC) bands. ...
Dislocations Gliding Study by IR Thermography in C-Mn Steels with Different Solute Atoms Content in the Gigacycle Fatigue Domain HUANG, Zhi Yong; RANC, Nicolas; WAGNER, Danièle (Trans Tech Publications, 2015)Tests were performed on two Carbon-Manganese steels (A42 and A48 steels, French standard) in the gigacycle fatigue domain thanks to a piezoelectric fatigue machine working at 20000Hz. During the tests, temperature recordings ...
A new piezoelectric fatigue testing machine in pure torsion for ultrasonic gigacycle fatigue tests: application to forged and extruded titanium alloys NIKITIN, Alexander; BATHIAS, Claude; PALIN-LUC, Thierry (Wiley, 2015)This article briefly discusses the history of the development of ultrasonic fatigue testing methods, with respect to industrial needs. The development of ultrasonic techniques and the progress made in the computer industry ...
Fatigue crack initiation and growth on a steel in the very high cycle regime with sea water corrosion PALIN-LUC, Thierry; PÉREZ-MORA, Ruben; BATHIAS, Claude; DOMINGUEZ, Gonzalo; PARIS, Paul C.; ARANA, Jose Luis (Elsevier, 2010)This paper is devoted to the effect of corrosion on the gigacycle fatigue strength of a martensitic–bainitic hot rolled steel used for manufacturing offshore mooring chains for petroleum platforms. Smooth specimens were ...