Fatigue Damage Initiation of a PA66/Glass Fibers Composite Material
TypeArticles dans des revues avec comité de lecture
Fatigue damage initiation of a PA66/glass fiber composite material is studied with interrupted tests carried out with an “alternative bending device” and a small applied strain. During the damage initiation period, no change of macroscopic properties, density, cristallinity ratio, glass transition temperature, and flexural elastic modulus is observed. Polysequential tests are carried out with three rest times differing by their length. These rest times allow the relaxation of macromolecular chains in the region of the microdefects and increase the number of cycles at fracture. The most efficient stop is the one just before the final fracture. The comparison of the fatigue behavior of the composite and its neat matrix shows that the microdefects relaxed during the break are identical to those which initiate damage and final fracture.
Showing items related by title, author, creator and subject.
ESMAEILLOU, Bardia; FERREIRA, Paulo; BELLENGER, Véronique; TCHARKHTCHI, Abbas (WILEY, 2012)In this study, the fatigue behavior of polyamide 66 reinforced with short glass fibers and especially the role of glass fibers has been investigated under two kinds of cyclic loading. tension–tension fatigue tests with ...
TCHARKHTCHI, Abbas; FARZANEH, Sedigheh; ABDALLAH-ELHIRTSI, Sofiane; ESMAEILLOU, Bardia; NONY, Fabien; BARON, A (Taylor & Francis Online, 2014)This study concerns the effect of thermal aging on mechanical properties of polyurethane. Polyurethane samples were exposed at 85° and 120°C under inert atmosphere. Mechanical tests were carried out on these samples the ...
Micro-mechanisms of fatigue in short glass fiber reinforced polyamide 66: A multi-scale experimental analysis ESMAEILLOU, Bardia; FITOUSSI, Joseph; MERAGHNI, Fodil; TCHARKHTCHI, Abbas (2014)The objective of this work is to identify and to analyze the main micro-mechanisms which govern the fatigue behavior of a short glass fiber reinforced polyamide 66 composite through a multi-scale experimental analysis. ...
MOUNIF, Eskandar; BELLENGER, Véronique; MAZABRAUD, Philippe; NONY, Fabien; TCHARKHTCHI, Abbas (Wiley, 2010)The identification of kinetic parameters controlling the crosslinking of Diglycidyl ether of bisphenol/isophorone diamine reactive system was achieved via optimization program (Inverse method) based on Fourier transform ...
DU, Weiwei; DOUADJI, Lyes; DELMOTTE, Michel; MAZABRAUD, Philippe; TCHARKHTCHI, Abbas (Société Française de Thermique / Congrès Français de Thermique, 29 mai - 1 juin 2007, Île des Embiez, 2007)Dans le procédé du rotomoulage, le phénomène physique majeur lors de l’écoulement des poudres est la coalescence et densification des grains. La coalescence est la formation d’une seule particule elliptique à partir de ...