Oxidative solution polymerization of aniline hydrochloride onto electrospun nanofibers mats of polylactic acid: Preparation method and characterization
TypeArticles dans des revues avec comité de lecture
In this work, we present the preparation of polylactic acid (PLLA)/polyaniline (PANI) conductive composite nanofibers mats. They are prepared by bulk oxidative solution polymerization of PANI onto electrospun non-woven fibers mats of PLLA. The PANI ratio in the composite is about 70%w/w. Scanning electron microscopy (SEM) shows that PLLA nanofibers are randomly oriented, beads free with diameters of 186 ± 85 nm, The PLLA/PANI composite nanofibers diameter values are 518 ± 128 nm with a good adherence between PANI and PLLA nanofibers. DSC and XRD measurements reveal an amorphous structure of the electrospun PLLA fibers due to the rapid evaporization of the solvent. FTIR and UV-vis spectra reflect good mutual interactions between PANI and PLLA chains. The DC-conductivities (σ=0.07-0.13-S.cm-1) far better than other published ones for similar composites prepared by bulk oxidative solution polymerization of PANI onto other electrospun nanofiber mats or with electrospun nanofibers from a solution mixture of PLLA and PANI.
Showing items related by title, author, creator and subject.
ESMAEILLOU, Bardia; FEREIRRA, P; BELLENGER, Véronique; TCHARKHTCHI, Abbas (Wiley, 2012)Fatigue damage initiation of a PA66/glass fiber composite material is studied with interrupted tests carried out with an “alternative bending device” and a small applied strain. During the damage initiation period, no ...
DU, Weiwei; DOUADJI, Lyes; DELMOTTE, Michel; MAZABRAUD, Philippe; TCHARKHTCHI, Abbas (Société Française de Thermique / Congrès Français de Thermique, 29 mai - 1 juin 2007, Île des Embiez, 2007)Dans le procédé du rotomoulage, le phénomène physique majeur lors de l’écoulement des poudres est la coalescence et densification des grains. La coalescence est la formation d’une seule particule elliptique à partir de ...
ABDALLAH-ELHIRTSI, Sofiane; FITOUSSI, Joseph; RASHMI, Baralu-Jagannatha; PRASHANTHA, Kalappa; FARZANEH, Sedigheh; LACRAMPE, Marie-France; KRAWCZAK, Patricia; TCHARKHTCHI, Abbas (Wiley Online Library, 2015)In this work, an experimental investigation on a partial shape memory polymer (PSMP) which is transformed into shape memory material is presented. Multicycle shape memory tests are performed on thermoplastic polyurethane ...
TCHARKHTCHI, Abbas; ABDALLAH-ELHIRTSI, Sofiane; EBRAHIMI, Kambiz; FITOUSSI, Joseph; SHIRINBAYAN, Mohammadali; FARZANEH, Sedigheh (MDPI, 2014)In this study some new concepts regarding certain aspects related to shape memory polymers are presented. A blend of polylactic acid (PLA) (80%) and polybutylene succinate (PBS) (20%) was prepared first by extrusion, then ...
SHIRINBAYAN, Mohammadali; FITOUSSI, Joseph; MERAGHNI, Fodil; SUROWIEC, Benjamin; BOCQUET, Michel; TCHARKHTCHI, Abbas (2015)Advanced Sheet Molding Compound (A-SMC) is a serious composite material candidate for structural automotive parts. It has a thermoset matrix and consists of high weight content of glass fibers (50% in mass) compared to ...