Internal Stress Analysis for the Damage Study of a 16MND5 Bainitic Steel
Article dans une revue avec comité de lecture
Date
2002Journal
Materials Science ForumAbstract
The behavior and the fracture mechanisms of the 16MND5 bainitic pressure vessel steel are studied using a local approach of fracture on a crystallographic scale. A series of tensile tests are performed on the material at various temperatures ranging from - 96°C to -60°C: the damage is observed with a Scanning Electron Microscope (SEM) while the residual stresses in the ferritic phase are determined by using the X-Ray Diffraction (XRD), never exceeding -150 MPa in compression. Thanks to these measurements, each stress value can be associated with a microscopie observation in order to couple the behavior of the material with the damage at various temperatures.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lectureINAL, Karim; PESCI, Raphaël; LEBRUN, Jean-Lou; DIARD, Olivier; MASSON, Renaud (Wiley-Blackwell, 2006)Stress analyses by X-ray diffraction are performed on a cast duplex (32% ferrite) stainless steel elbow and a bainitic (95% ferrite) pressure vessel steel. During an in situ tensile test, micrographic observations are made ...
-
Article dans une revue avec comité de lecturePESCI, Raphaël; INAL, Karim; BERVEILLER, Marcel; MASSON, Renaud (Elsevier, 2003)La nature biphasée de l’acier bainitique 16MND5 (ferrite/cémentite) fait de la Diffraction des Rayons X (DRX) l’outil privilégié pour déterminer les états de contrainte dans la phase ferritique (méthode des sin2 ψ). Couplés ...
-
Article dans une revue avec comité de lecturePESCI, Raphaël; INAL, Karim; BERVEILLER, Sophie; PATOOR, Etienne; LECOMTE, Jean-Sébastien; EBERHARDT, André (Trans Tech Publications Inc, 2006)A Kossel microdiffraction experimental set up is under development inside a Scanning Electron Microscope (SEM) in order to determine the crystallographic orientation as well as the inter- and intragranular strains and ...
-
Conférence invitéeDIARD, Olivier; MATHIEU, Jean-Philippe; STUDER, Vincent; PESCI, Raphaël; INAL, Karim (2005)A specific in-situ tensile device has been set up in an X-Ray diffractometer. Stress can be measured at low temperature during loading in the baintic steel and in the ferritic phase. A two-scale modeling has been proposed ...
-
Article dans une revue avec comité de lecturePESCI, Raphaël; INAL, Karim; MASSON, Renaud (Elsevier, 2004)Many tensile tests have been realized on the 16MnNiMo5 bainitic pressure vessel steel at low temperatures [-196°C, -60°C]. The damaging processes (ductile/fragile) are observed with a scanning electron microscope (SEM), ...