Fatigue crack initiation and growth in a 35CrMo4 steel investigated by infrared thermography
TypeArticles dans des revues avec comité de lecture
The present work is devoted to the investigation of fatigue crack initiation and growth in middle-cycle fatigue (∼105 cycles). Smooth specimens made of 35CrMo4 quenched and tempered steel were loaded in fully reversed plane bending. Temperature field evolution in time was recorded with an infrared camera. The experimental results show that the local heating of metal under fatigue loading is a sensitive and accurate enough manifestation of small fatigue crack initiation. It is shown that the time evolution of the spatial standard deviation of the temperature field can be used to investigate the damage localization and to monitor both the crack initiation and the current location of the fatigue crack tip. This should help to investigate the behaviour of defect during cyclic loading.
Showing items related by title, author, creator and subject.
Experimental Investigations of Anomalous Energy Absorption in Nanocrystalline Titanium under Cyclic Loading Conditions PLEKHOV, O.A; NAIMARK, O.B; VALIEV, R.Z; SEMENOVA, I.P; SAINTIER, Nicolas; PALIN-LUC, Thierry (Wiley, 2008)An infrared thermographic scanning technique has been used to study the energy absorption and dissipation under cyclic loading conditions in the nanostructural bulk titanium obtained by severe plastic deformation of an ...
PLEKHOV, O.A; NAIMARK, O.B; SAINTIER, Nicolas; PALIN-LUC, Thierry (Pleiades Publishing, 2009)The structural and thermodynamic features of the elastic–plastic transition in armco iron and its plastic deformation are studied. Energy storage in iron is shown to have a nonlinear character and be accompanied by wavelike ...
Theoretical analysis, infrared and structural investigations of energy dissipation in metals under cyclic loading PLEKHOV, O.A; SAINTIER, Nicolas; PALIN-LUC, Thierry; UVAROV, S. V.; NAIMARK, O.B (Elsevier, 2007)The infrared and structural investigations of energy dissipation processes in metals subjected to cyclic loading have given impetus to the development of a new thermodynamic model with the capability of describing the ...
Experimental and Theoretical Study of Multiscale Damage-Failure Transition in Very High Cycle Fatigue BETEKHTIN, V.I.; KADOMTSEV, A.G.; NARYKOVA, M.V.; BANNIKOV, M.V.; ABAIMOV, S.G.; AKHATOV, I. S.; PALIN-LUC, Thierry; NAIMARK, O.B (Pleiades, 2017)Multiscale mechanisms of failure of metals (Armco iron, titanium, aluminum) are studied for high cycle and very high cycle fatigue. By correlating with the results of structural studies, a theoretical approach is developed ...
OBORIN, V.; BANNIKOV, M.V.; NAIMARK, O.B; PALIN-LUC, Thierry (Pleiades Publishing, 2010)The role of the collective behavior of defect ensembles at the crack tip and the laws of fatigue crack propagation in R4 high strength steel have been studied under conditions of symmetric tension–compression gigacycle ...