Sliding wear behavior of magnetron sputtered chromium carbide thin films
Article dans une revue avec comité de lecture
Purpose – The purpose of this technical paper is to investigate the friction and wear behavior of inexpensive and durable cutting tools, developed for wood machining using duplex treatment. Design/methodology/approach – Cr–(WC–Co) coatings were eposited onto carburized low-alloy steel substrate by a reactive magnetron sputtering. The total coating thickness was approximately 2 m. Unlubricated wear tests have been performed using a disc sample sliding against an alumina ball (Al2O3) and a wood (beech) pin. Findings – The paper provides information about the effect of duplex reatment on the surface properties of low-alloy steel against wood and offers practical help for the researchers in coating topic. Originality/value – Experimental results showed that sliding wear properties of the selected coatings are strongly dependent on the counter-face material. When tested against alumina balls, the wear mechanisms are oxidative wear followed by a combination of adhesive and abrasive wear, while a combination of an oxidative and adhesive wear was the main wear mechanism observed against a wood pin.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Visualiser des documents liés par titre, auteur, créateur et sujet.
Article dans une revue avec comité de lectureBELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Scientific Bulgarian Communications Ltd, 2014)The sliding tribological behaviour of Cr-(WC-Co) coating against wood (beech) as counterpart was investigated using a duplex treatment of low carbon steel(DIN 18CrMo4). The duplex treatment consists of LPC (low pressure ...
Article dans une revue avec comité de lectureRAMOUL, Chams Eddine; BELIARDOUH, Nasser Eddine; BAHI, R.; NOUVEAU, Corinne; DJAHOUDI, Abdelghani; WALOCK, Michael J. (2018)Zirconium nitride (ZrN) thin films were deposited by reactive RF magnetron sputtering on Ti-6Al-4V and Si (100) substrates for potential use in biomedical applications. The tribological behaviour was evaluated against ...
Tribological and electrochemical performances of Cr/CrN and Cr/CrN/CrAlN multilayer coatings deposited by RF magnetron sputtering Article dans une revue avec comité de lectureBELIARDOUH, Nasser Eddine; BOUZID, Kheireddine; NOUVEAU, Corinne; TLILI, Brahim; WALOCK, Michael J. (Elsevier, 2015)CrN/CrAlN and Cr/CrN/CrAlN multilayers were grown with dual RF magnetron sputtering. The application of these multilayers will be wood machining of green wood. That is why ball-on-disc and electrochemical tests in NaCl ...
Article dans une revue avec comité de lectureBOUZID, Kheireddine; BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne (the Serbian Tribology Society, 2015)A comparative study was conducted to evaluate the performances against wear and corrosion of CrN, CrMoN, CrZrN, CrVN single layer thin films. The latest are synthesized onto steel substrates (DIN 90CrMoV8), using R.F ...
A study of the wear performance of duplex treated commercial low-alloy steel against alumina and WC balls Article dans une revue avec comité de lectureBELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; WALOCK, Michael J.; JACQUET, Philippe (Elsevier, 2014)The objective of this work is to study the improvement of the tribological properties of low alloy steel using a duplex treatment of lowpressure carburizing and the deposition of a Cr–(WC–Co) coating by dual RF magnetron ...