Dry sliding wear investigation on tungsten carbide particles reinforced iron matrix composites
TypeArticles dans des revues avec comité de lecture
WCparticles reinforced Fe-based metal matrix composites were synthesized by powder metallurgy process. The microstructure and composition of the specimens were analyzed and the wear-resistant properties againstWCand alumina balls were comparatively investigated by SEM/EDS analyses. The wear rates of specimens were evaluated by optical profilometry. Microstructure exhibited austenite Fe-FCC dendrites, eutectic (iron austenite + carbides) and primary carbides. Two wear mechanisms have been identified from SEM as main mechanisms during dry sliding wear of Tungsten carbides reinforced iron matrix, namely oxidation and abrasion. The overall wear performance, which is obtained by considering the wear loss of the substrates, indicated less resistance against Alumina compared to WC ball contact.
Files in this item
Showing items related by title, author, creator and subject.
Tribological and electrochemical performances of Cr/CrN and Cr/CrN/CrAlN multilayer coatings deposited by RF magnetron sputtering BELIARDOUH, Nasser Eddine; BOUZID, Kheireddine; NOUVEAU, Corinne; TLILI, Brahim; WALOCK, Michael J. (Elsevier, 2015)CrN/CrAlN and Cr/CrN/CrAlN multilayers were grown with dual RF magnetron sputtering. The application of these multilayers will be wood machining of green wood. That is why ball-on-disc and electrochemical tests in NaCl ...
BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Scientific Bulgarian Communications, 2014)The sliding tribological behaviour of Cr-(WC-Co) coating against wood (beech) as counterpart was investigated using a duplex treatment of low carbon steel(DIN 18CrMo4). The duplex treatment consists of LPC (low pressure ...
BOUZID, Kheireddine; BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne (University of Kragujevac, 2015)A comparative study was conducted to evaluate the performances against wear and corrosion of CrN, CrMoN, CrZrN, CrVN single layer thin films. The latest are synthesized onto steel substrates (DIN 90CrMoV8), using R.F ...
A study of the wear performance of duplex treated commercial low-alloy steel against alumina and WC balls BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; WALOCK, Michael J.; JACQUET, Philippe (elsevier, 2014)The objective of this work is to study the improvement of the tribological properties of low alloy steel using a duplex treatment of lowpressure carburizing and the deposition of a Cr–(WC–Co) coating by dual RF magnetron ...
BELIARDOUH, Nasser Eddine; NOUVEAU, Corinne; KALELI, Hakan (Emerald Group, 2016)Purpose – The purpose of this technical paper is to investigate the friction and wear behavior of inexpensive and durable cutting tools, developed for wood machining using duplex treatment. Design/methodology/approach – ...