The influence of veneer thickness and knot proportion on the mechanical properties of laminated veneer lumber (LVL) made from secondary quality hardwood
TypeArticles dans des revues avec comité de lecture
The first objective of this work was to study the influence of veneer quality on the mechanical properties of laminated veneer lumber (LVL) made of secondary quality hardwood. The second objective was to propose an adapted veneer thickness that provides the optimum mechanical properties of LVL, taking the veneer properties into account. Forty-eight LVL panels glued together using polyvinyl acetate (PVAc) were prepared. The quality of fresh veneers was assessed by measuring veneer knot proportion, lathe check depth and lathe check interval. The static modulus of elasticity (MOE), dynamic MOE, modulus of rupture (MOR) and shear modulus were measured using destructive and non-destructive methods. The 3 mm thick veneer provided the optimum mechanical properties for LVL for both species. The test direction did not have any significant influence on the mechanical properties. In the flatwise direction, the average MOE values obtained were 13.2 GPa for beech LVL and 13.3 GPa for oak LVL, whereas the MOR was 72.0 MPa and 63.4 MPa, respectively. Increasing knot proportion in veneers results in a decrease in LVL MOE and MOR. Moreover, deeper lathe checks and higher lathe check intervals on veneer surfaces provide lower LVL shear modulus in the edgewise direction for both species. Internal veneer provides LVL with a higher density but weaker mechanical properties due to a higher knot proportion in the internal veneer.
Files in this item
Showing items related by title, author, creator and subject.
An innovative method based on grain angle measurement to sort veneer and predict mechanical properties of beech laminated veneer lumber VIGUIER, Joffrey; BOURGEAY, Christophe; ROHUMAA, Anti; POT, Guillaume; DENAUD, Louis (Elsevier, 2018)This study proposes an innovative model based on local grain angle measurements to predict the modulus of elasticity of LVL made from beech. It includes a veneers sorting method industrially compatible thanks to its low ...
Modelling mechanical properties of spruce and Douglas fir timber by means of X-ray and grain angle measurements for strength grading purpose VIGUIER, Joffrey; BOURREAU, Damien; BOCQUET, Jean-François; POT, Guillaume; BLERON, Laurent; LANVIN, Jean-Denis (Springer, 2017)This study proposes a model using data from a scanner (X-ray and grain angle measurements) to perform strength grading. The research also includes global measurements of modulus of elasticity (obtained by vibrations and ...
BESSEAU, Benoît; POT, Guillaume; COLLET, Robert; VIGUIER, Joffrey (2019)Scanner measurements allow knot detection and machine strength grading on sawn timber, which answers the construction and sawmilling industry needs at high production rates. In particular, laser scanners measure fiber ...
Performance of strength grading methods based on fibre orientation and axial resonance frequency applied to Norway spruce (Picea abies L.), Douglas fir (Pseudotsuga menziesii (Mirb.) Franco) and European oak (Quercus petraea (Matt.) Liebl./Quercus robur L.) OLSSON, Anders; POT, Guillaume; VIGUIER, Joffrey; FAYDI, Younes; OSCARSSON, Jan (Springer Nature, 2018)Key message Machine strength grading of sawn timber is an important value adding process for the sawmilling industry. By utilizing data of local fibre orientation on timber surfaces, obtained from laser scanning, more ...
Assessment of the error of fiber orientation measurement obtained by laser scanning on several European hardwood and softwood species BESSEAU, Benoît; POT, Guillaume; VIGUIER, Joffrey; COLLET, Robert (CompWood 2019 Conference, 2019)Scanner measurements allow knot detection and machine strength grading on sawn timber. In particular, laser scanners measure fiber orientation by means of the so-called tracheid effect explained by the fact that the wood ...