Microstructure-based study of the crack initaition mechanisms in pure copper under high cycle multiaxial fatigue loading conditions
Type
Articles dans des revues avec comité de lectureDate
2016Journal
Procedia Structural IntegrityAbstract
This paper aims to contribute in understanding the fatigue crack initiation mechanisms in metallic materials under high cycle multiaxial fatigue loadings. It addresses proportional and non-proportional multiaxial loading conditions with the analysis and observation of the cyclic plasticity development (mainly persistent slip band) until crack initiation (especially short cracks) on a pure oxygen-free high conductivity (OFHC) polycristalline copper. Observation and analysis techniques are based mainly on optical microscopy and scanning electron microscopy (SEM). It has been observed that the plastic slip multiplicity in grains seems more important for multiaxial loadings at a stress level corresponding to the same median fatigue strength at 106 cycles of the material. A multiaxial loading induces an additional multiplicity of the plastic slip in grains compared to uniaxial loading condition. For all the loading conditions investigated, although most of the grains exhibits single slip activated, analysis of the preferential crack initiation sites and modes show a higher probability of intragranular microcrack initiation in the multiple slip grains (with more than two slip systems activated). Most multiple slip grains and higher probability of crack initiation in these grains were observed especially for non-proportional multiaxial loadings. Finally, the effects of the biaxiality ratio and the phase shift on the fatigue crack initiation was highlighted.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
MESSAGER, Alexandre; JUNET, Arnaud; PALIN-LUC, Thierry; BUFFIÉRE, Jean Yves; SAINTIER, Nicolas; RANC, Nicolas; EL MAY, Mohamed; GAILLARD, Yves; KING, Andrew; BONNIN, Anne; NADOT, Yves (2020)This work presents a new ultrasonic fatigue testing device for studying the initiation and propagation mechanisms of internal microstructurally short fatigue cracks using in situ synchrotron tomography. Its principle is ...
-
RANC, Nicolas; PALIN-LUC, Thierry; PARIS, Paul Croce; SAINTIER, Nicolas (ELSEVIER, 2014)Because of the reverse cyclic plastic zone at the crack tip, there is plastic dissipation in heat at the crack tip under cyclic loading. That creates a heterogeneous temperature field around the crack tip. A thermomechanical ...
-
RANC, Nicolas; PALIN-LUC, Thierry; PARIS, Paul Croce; SAINTIER, Nicolas (Elsevier, 2013)Because of the reverse cyclic plastic zone at the crack tip, there is plastic dissipation in heat at the crack tip under cyclic loading. That creates a heterogeneous temperature field around the crack tip. A thermo-mechanical ...
-
Non-local energy based fatigue life calculation method under multiaxial variable amplitude loadings SAINTIER, Nicolas; PALIN-LUC, Thierry; BÉNABÈS, Jérôme; COCHETEUX, Francis (Elsevier, 2013)Reliable design of industrial components against high cycle multiaxial fatigue requires a model capable of predicting both stress gradient and load type effects. Indeed, taking into account gradient effects is of prior ...
-
ROBERT, Camille; HOR, Anis; MOREL, Franck; SAINTIER, Nicolas; PALIN-LUC, Thierry (2013)An analysis of high cycle fatigue behavior is done via the numerical simulation of polycrystalline aggregates. Different metallic materials with a FCC crystalline structure, but different cubic elastic coefficients, are ...