Hot dwell-fatigue behaviour of additively manufactured AlSi10Mg alloy: Relaxation, cyclic softening and fracture mechanisms
Article dans une revue avec comité de lecture
This paper presents the results of high temperature strain-range controlled low cycle fatigue tests of a laser powder bead fused AlSi10Mg alloy. Following stress relief (2hrs at 300 ℃), two cyclic loading waveforms (standard triangular and dwell-type trapezoidal waveforms) and three temperatures (100 ℃, 250 ℃ and 400 ℃) were applied to investigate both the mechanical response and the related microstructural changes of this additively manufactured (AM) aluminium alloy. The bulk mechanical responses were found to exhibit a continuous cyclic softening, decreasing stress relaxation and decreased energy dissipated per cycle. The stress relaxation is strongly affected by the test temperature rising to almost complete relaxation at 400 ℃. At lower temperatures (100 ℃ and 250 ℃), the higher the temperature the more subgrains are developed during cyclic loading. Up to 250 ℃, the subgrain size increases with temperature and laser powder bead fused defects preferentially act as the fatigue crack initiation sites. While at 400 ℃, coarse Si particles precipitate during cyclic deformation and a high density of microvoids are nucleated from these coarse Si precipitates, which grow and link up to cause failure, resulting in a dimple dominated ductile fracture.
Files in this item
Showing items related by title, author, creator and subject.
High temperature strain heterogeneities tracking within hole-specimens of fv566 turbine steel via digital image correlation Article dans une revue avec comité de lectureBAO, Jianguang; BENAARBIA, Adil; BAO, Siyuan; GUO, Xiaofeng; WANG, Yonghong; SUN, Wei (Elsevier, 2020)This paper presents experimental and numerical investigations to study spatial-temporal distributions of strain heterogeneities within a FV566 turbine rotor steel subjected to high temperature conditions. Strain field were ...
Experimental characterisation and computational modelling of cyclic viscoplastic behaviour of turbine steel Article dans une revue avec comité de lectureRAE, Yaroslav; BENAARBIA, Adil; HUGUES, Jeremy; SUN, Wei (Elsevier, 2019)Fully reversed strain controlled low cycle fatigue and creep-fatigue interaction tests have been performed at ±0.7% strain amplitude and at three different temperatures (400°C, 500°C and 600°C) to investigate the cyclic ...
Characterization of cyclic behavior, deformation mechanisms, and microstructural evolution of MarBN steels under high temperature conditions Article dans une revue avec comité de lectureBENAARBIA, Adil; XU, Xu; SUN, Wei; BECKER, Adib; OSGERBY, Steve (Elsevier, 2019)In this paper, the low cycle fatigue behaviour of MarBN steels at elevated temperatures is discussed. Four cyclic loading waveforms were applied to investigate both the mechanical and microstructural features. The mechanical ...
On the microstructural evolution in 12% Cr turbine steel during low cycle fatigue at elevated temperature Article dans une revue avec comité de lectureRAE, Yaroslav; GUO, X.; BENAARBIA, Adil; NEATE, Nigel; SUN, Wei (Elsevier, 2020)In order to better understand the physical process of deformation and cyclic softening a 12% Cr martensitic stainless steel FV566 has been cyclically tested at high temperature in strain control. Increase in temperature ...
Assessment of potential service-life performance for MarBN steel power plant header under flexible thermomechanical operations Article dans une revue avec comité de lectureLI, M.; BENAARBIA, Adil; MORRIS, A.; SUN, W. (Elsevier, 2020)This paper is concerned with the service-life assessment of 9Cr steels superheater outlet steam header subjected to realistic subcritical and future ultra-super critical flexible operating conditions. The proposed methodology ...