Detrimental effect of high-productivity L-PBF parameters on metal dusting resistance of Inconel 625
Article dans une revue avec comité de lecture
Author
VERNOUILLET, Annabelle 
VANDE PUT, Aurélie PUGLIARA, Alessandro EPIFANO, Enrica DE TERRIS, Thibaut PEYRE, Patrice DOUBLET, Solène MONCEAU, DanielAbstract
The effect of increased productivity in L-PBF manufacturing on the metal dusting resistance of Inconel 625 was studied at 610 ◦C. Two sets of processing parameters were tested: the standard parameters given by the machine manufacturer and degraded parameters with increased scan speed and hatching distance. The materials obtained with degraded parameters presented numerous lacks of fusion at the surface and exhibited significantly shorter incubation times before corrosion. Carburisation was preferentially localised around the defects where the oxide scale was less protective and where the confinement of the atmosphere could result in an increase of the local carbon activity.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Texture control of 316L parts by modulation of the melt pool morphology in selective laser melting Article dans une revue avec comité de lecture; ; ; ; ; ;KOUTIRI, Imade; PESSARD, Etienne; SAINTIER, Nicolas (Elsevier, 2019)
In this study, 316L parts were fabricated with the selective laser melting additive layer manufacturing process using unidirectional laser scan to control their texture. The melt pool shape, microstructure and texture of ...
-
Article dans une revue avec comité de lecture(Elsevier, 2020)The use of large beams in the Laser Powder Bed Fusion (L-PBF) process has been receiving increasing attention for the past few years and may widen the dissemination of this technology in the industry, as well as help ...
-
Article dans une revue avec comité de lecture; ; ; ; ; ;KOUTIRI, Imade (Elsevier, 2019)
The systematic occurrence of porosities inside selective laser melted (SLM) parts is a well-known phenomenon. In order to improve the density of SLM parts, it is important not only to assess the physical origin of the ...
-
Article dans une revue avec comité de lecture; ; ;HADDADI, Halim; ; (MDPI AG, 2021)
The microstructures induced by the laser-powder bed fusion (L-PBF) process have been widely investigated over the last decade, especially on austenitic stainless steels (AISI 316L) and nickel-based superalloys (Inconel ...
-
Article dans une revue avec comité de lectureKOUTIRI, Imade; PESSARD, Etienne; ; ; (Elsevier, 2018)
This paper is dedicated to understanding fatigue crack initiation for an Inconel 625 manufactured by SLM, using a hatching + contour procedure. In the first part of the paper, an optimum set of parameters was found to ...