Prediction of microgeometrical influences on micropitting fatigue damage on 32CrMoV13 steel
Article dans une revue avec comité de lecture
Micropitting is a form of surface fatigue damage that occurs in the gear teeth. It is due to the effect of variation in the mechanical loading in the contact zone between the two teeth, induced especially by flank roughness. In this study, generic roughness profiles were built with geometrical parameters to simulate the contact between two rough surfaces. Using elastohydrodynamic lubrication code and Crossland’s fatigue criteria, the influence on fatigue lifetime was analysed for changes in each parameter. The relevant parameters were determined that influence(i) the conventional pitting,(ii) the extent to which the von Mises equivalent stress exceeds the material yield stress in the zone where micropitting occurs, and(iii) the fatigue lifetime for steel teeth. With nitriding benefits, the same trends were shown with weaker effects.
Showing items related by title, author, creator and subject.
Communication sans acteFABRE, Agnès; JEGOU, Sébastien; BARRALLIER, Laurent (2014)Le rodage est un phénomène présent lors des premiers cycles de frottement qui modifie la surface de contact d’une pièce d’un point de vue géométrique, couplé à des modifications de propriétés mécaniques. Le rodage génère ...
Communication sans acteJEGOU, Sébastien; BARRALLIER, Laurent; FABRE, Agnès (2014)In a previous study, the capability of X-ray diffraction technique to qualify damage occurring during friction had been proven . The purpose of this study is to complete this research in order to develop a method to ...
A Thermodynamic and experimental study of low-alloy steels after carbonitriding in a low-pressure atmosphere Article dans une revue avec comité de lectureMARRAY, Tarek; JACQUET, Philippe; MANSORI, Mohammed; FABRE, Agnès; BARRALLIER, Laurent (Springer Verlag, 2014)The effect of the composition of two steels (B and 6MnCr5) on precipitation of undesirable phases (carbides, nitrides and carbonitrides) under thermochemical treatment (low-pressure or vacuum carbonitriding) is investigated. ...
Communication sans acteFABRE, Agnès; JEGOU, Sébastien; BARRALLIER, Laurent (2014)In a previous study, the capability of X-ray diffraction technique to qualify damage occurring during friction had been proven . The purpose of this study is to complete this research in order to develop a method to ...
Conférence invitéeFABRE, Agnès (2015)This keynote is a review of previous works on the measurement of the roughness, on the influence of roughness on the fatigue lifetime of gears, on an investigation. This presentation deals first with the development of ...