Qualification of the damage induced by friction using X-ray Diffractometry
Communication sans acte
Auteur
FABRE, AgnèsBARRALLIER, Laurent 
JÉGOU, SébastienRésumé
In a previous study, the capability of X-ray diffraction technique to qualify damage occurring during friction had been proven [1]. The purpose of this study is to complete this research in order to develop a method to quantify the damage induced by the friction loading.
Fichier(s) constituant cette publication
Cette publication figure dans le(s) laboratoire(s) suivant(s)
Documents liés
Visualiser des documents liés par titre, auteur, créateur et sujet.
-
Communication sans acte; ;JÉGOU, Sébastien (2014)
Le rodage est un phénomène présent lors des premiers cycles de frottement qui modifie la surface de contact d’une pièce d’un point de vue géométrique, couplé à des modifications de propriétés mécaniques. Le rodage génère ...
-
Communication sans acte; ;JÉGOU, Sébastien (2014)
In a previous study, the capability of X-ray diffraction technique to qualify damage occurring during friction had been proven [1]. The purpose of this study is to complete this research in order to develop a method to ...
-
Article dans une revue avec comité de lecture(Elsevier, 2013)Micropitting is a form of surface fatigue damage that occurs in the gear teeth. It is due to the effect of variation in the mechanical loading in the contact zone between the two teeth, induced especially by flank roughness. ...
-
Article dans une revue avec comité de lecture(Springer Verlag, 2014)The effect of the composition of two steels (B and 6MnCr5) on precipitation of undesirable phases (carbides, nitrides and carbonitrides) under thermochemical treatment (low-pressure or vacuum carbonitriding) is investigated. ...
-
Article dans une revue avec comité de lecture; ;JÉGOU, Sébastien; KUBLER, Regis (Hanser, 2011)
Development and evolution of compressive residual stress during nitriding treatment are studied. A model carbon iron-based alloy Fe-3wt.%Cr-0.35wt.%C was nitrided in gas at 550 °C for different times. Microstructural ...