The behavior of statically-indeterminate structural members and frames with cracks present
Date
2009Journal
Engineering Fracture MechanicsAbstract
Crack stability is discussed as affected by their presence in statically-indeterminate beams, frames, rings, etc. loaded into the plastic range. The stability of a crack in a section, which has become plastic, is analyzed with the remainder of the structure elastic and with subsequent additional plastic hinges occurring. The reduction of energy absorption characteristics for large deformations is also discussed. The methods of elastic–plastic tearing instability are incorporated to show that in many cases the fully plastic collapse mechanism must occur for complete failure.
Files in this item
Related items
Showing items related by title, author, creator and subject.
-
Article dans une revue avec comité de lectureThis paper is focused on the effect of sea water corrosion on the gigacycle fatigue strength of a martensitic–bainitic hot rolled steel R5 used for manufacturing off-shore mooring chains for petroleum platforms in the North ...
-
Article dans une revue avec comité de lecturePlastic dissipation at the crack tip under cyclic loading is responsible for the creation of an heterogeneous temperature field around the crack tip. A thermomechanical model is proposed in this paper for the theoretical ...
-
Article dans une revue avec comité de lecturePALIN-LUC, Thierry; PÉREZ-MORA, Ruben; BATHIAS, Claude; DOMINGUEZ, Gonzalo; PARIS, Paul Croce; ARANA, Jose Luis (Elsevier, 2010)This paper is devoted to the effect of corrosion on the gigacycle fatigue strength of a martensitic–bainitic hot rolled steel used for manufacturing offshore mooring chains for petroleum platforms. Smooth specimens were ...
-
Article dans une revue avec comité de lectureBecause of the reverse cyclic plastic zone at the crack tip, there is plastic dissipation in heat at the crack tip under cyclic loading. That creates a heterogeneous temperature field around the crack tip. A thermomechanical ...
-
Article dans une revue avec comité de lectureBecause of the reverse cyclic plastic zone at the crack tip, there is plastic dissipation in heat at the crack tip under cyclic loading. That creates a heterogeneous temperature field around the crack tip. A thermo-mechanical ...